Abstract:The aim of this work is to evaluate the influence of octene-1 incorporation in the polybutadiene chain on the polymerization reaction and polymer characteristics. Thus, copolymerization of butadiene-1,3 with octene-1 using a Ziegler-Natta ternary catalyst based on neodymium was performed. The weight ratios of butadiene-1,3/α-olefin 100/0, 99/1, 97/3, 95/5, 90/10, 80/20 and 70/30 were evaluated. The copolymers were characterized by size exclusion chromatography (SEC), infrared spectroscopy (FTIR) and thermogravimetric analysis (TG). The results showed that the degradation temperature (Tmax) was not affected by the addition of alpha-olefin, while the thermal behavior has undergone significant changes. The polymer microstructure was not influenced by the increasing of octene-1 content. However, a tendency to molecular mass increase was observed with the increasing of octene-1 content. It was also observed a trend in reduction of the polymerization conversion as the octene-1 content increased.
Resumo: A viscosimetria é um procedimento experimental simples e pouco oneroso, que pode fornecer informações valiosas sobre o volume hidrodinâmico e a conformação de macromoléculas em solução, num determinado solvente, em uma dada temperatura. Os parâmetros viscosimétricos podem ser matematicamente calculados por extrapolação gráfica, cuja execução experimental é mais demorada. Em contrapartida, é possível que a determinação seja feita por um único ponto. Foi realizado um estudo viscosimétrico, em solução, de polibutadieno e de copolímeros aleatórios de 1,3-butadieno e 1-octeno, (obtidos com diferentes razões, em massa, de 1,3-butadieno/1-octeno (Bd/Oct = 99/1 e 97/3) utilizando-se tolueno e hexano, a 30 ± 0,1 °C. A massa molar das amostras foi determinada por cromatografia de exclusão por tamanho (SEC). Os cálculos por extrapolação gráfica foram feitos empregando-se as equações de Huggins, Kraemer e Schulz-Blaschke e a determinação por único ponto pelas equações de Schulz-Blaschke, Solomon-Ciuta e Deb-Chanterjee. O método de determinação por um único ponto mostrou-se eficiente para os sistemas estudados. Avaliou-se a qualidade dos solventes por meio da determinação das constantes viscosimétricas de Huggins e Kraemer. Ambos os solventes utilizados podem ser classificados como bons para os polímeros analisados (k h <0,5 e k k <0), sendo o hexano o melhor, uma vez que as viscosidades intrínsecas determinadas para todas as amostras neste solvente foram maiores do que as determinadas em tolueno. Por meio dos valores de viscosidade intrínseca e do parâmetro g' (razão entre as viscosidades do polímero ramificado e do linear) foi confirmada a existência de ramificações na cadeia polimérica já que g'<1 e os valores de viscosidade intrínseca são inferiores aos obtidos para o homopolímero. Palavras-chave: Copolimerização, 1,3-butadieno, 1-octeno, viscosimetria, determinação por um único ponto. Viscosimetric Study of Copolymer Based on 1,3-Butadiene and 1-Octene in Toluene and HexaneAbstract: Viscosimetry is a simple, inexpensive characterization method that provides valuable information about the hydrodynamic volume and conformation of macromolecules in solution, in a solvent, at a given temperature. The viscosimetric parameters can be mathematically calculated by graphic extrapolation, in time-consuming experimental tests. It is possible, however, to achieve results by a single point determination. In this work we used the two calculation methods employing a series of six equations: Huggins, Kraemer and Schulz-Blaschke, by graphic extrapolation; and Schulz-Blaschke, Solomon-Ciuta and Deb-Chanterjee, by a single point determination, for solutions of polybutadiene and of random copolymers of 1,3-butadiene and 1-octene, with different mass ratios (Bd/Oct = 99/1 and 97/3). The viscosimetric determinations were carried out in toluene and hexane, at 30 ± 0.1 °C. The weight average molecular mass was determined by size exclusion chromatography (SEC). The values of intrinsic viscosity and of some constants indicated that both t...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.