PURPOSE This study aimed to compare the microshear bond strength (µSBS) of dual-cure resin cement in CAD-CAM zirconia after different cleaning techniques. MATERIALS AND METHODS Fifty discs of zirconia-based ceramic from Ivoclar Vivadent were embedded in acrylic resin. The discs were divided into five groups according to the cleaning methods used: Group 1: drying with spraying + sandblasting with Al 2 O 3 ; Group 2: washed with water and dried with spraying + sandblasting with Al 2 O 3 ; Group 3: washed with distilled water and dried with spraying + sandblasting with Al 2 O 3 + zirconium oxide (Ivoclean); Group 4: washed with distilled water and dried with spraying + sandblasting with Al 2 O 3 + potassium hydroxide (Zirclean); and Group 5: washed with distilled water and dried with spraying + sandblasting with Al 2 O 3 + 1% NaClO. All of the groups were contaminated with artificial saliva for 1 minute and then cleaned. Statistical analyses were performed using ANOVA and Tukey's tests. RESULTS There were statistically significant differences among all groups for µSBS ( P < .05). The group treated with zirconium oxide (Group 3) showed the highest µSBS (18.75 ± 0.23 MPa). CONCLUSION When applied to zirconia, the cleaning methods affected the bonding with resin cement differently.
En los años 90s, se empezó con el uso de la resina compuesta como agente cementante, la cual tiene como ventajas: un margen con alto contenido de relleno, facilidad de limpiar excesos antes de la polimerización, potencial de rellenar cualquier defecto en la preparación mejorando el sellado marginal, etc. Uno de las controversias de esta técnica, es la elevación de la temperatura intra pulpar, la cual, sumada al proceso de polimerización podría llegar a elevarse hasta causar algún daño irreversible, sin embargo, se ha demostrado, que la resina precalentada se enfría rápidamente, gracias a los tejidos dentarios que disipan el calor y al tiempo transcurrido de llevar la resina del horno a la boca. Con el calentamiento de las resinas, se produce una reducción de su viscosidad, permitiendo una menor formación de gaps y una mejor adaptación marginal, sin afectar las propiedades mecánicas de las resinas compuestas, esto ocurre debido al aumento de la movilidad molecular, las cuales optimizan sus propiedades mecánicas luego de la polimerización. Con respecto a las propiedades adhesivas los cementos resinosos y las resinas precalentadas han sido evaluadas mediante la fijación de las restauraciones indirectas a la estructura dentaria, obteniéndose con las resinas precalentada resultados favorables con relación a la filtración, resistencia adhesiva, pero en cuanto al grosor, el cemento resinoso genera una película más fina, sin embargo logra ser posible utilizar la resina precalentada como agente cementante como una técnica segura.
Aim: To compare the application of silane in the bond strength of fiberglass posts in different thirds of the cemented root with a self-adhesive system in an ex vivo study. Materials and methods: Freshly extracted teeth were collected, which had indication of extraction for periodontal or orthodontic reasons. The study evaluated n = 42 specimens that were divided into two large groups: I (control, without silane) and II (with silane); the resistance to adhesion in the respective thirds of the root (cervical, middle, and apical) was also evaluated. The prefabricated fiberglass posts were cemented with and without silane according to the manufacturer's instructions and were cemented with a resin-based cementing agent. The adhesion strength test was evaluated by the universal testing machine. Results: According to the results of this experimental trial, the fiberglass posts that did not receive silane had the highest adhesion strength of 26.5 ± 10.6 MPa, while silane-cemented posts only had 21.7 ± 8.1 MPa. The statistical analysis was performed using the Kruskal-Wallis test and work with a level of significance of p < 0.05. Conclusion:The use of silane as part of the cementing protocol in fiberglass posts does not influence the adhesion strength between the surfaces of the posts and the resin cement because there were statistically significant differences between both adhesion protocols. Clinical significance: This study has a great impact because according to the results, clinical decisions can be made when cementing the fiberglass posts through the application of silane or not.
Para el rehabilitador oral, resulta fundamental determinar con precisión la orientación del plano oclusal en pacientes con distintas alteraciones, como desgastes severos, edentulismo parcial, total y sus consecuencias. Es importante que este sea lo más cercano posible a la posición queocupaba en dentición natural, ya que influye principalmente en la función oclusal, de los músculos masticatorios, en la articulación temporomandibular, en la fonética y en la estética. Además, la correcta determinación constituye la base de la planificación, por ser el plano de referencia estético y funcional; determina la guía anterior, los patrones de movimiento mandibular, la eficiencia masticatoria y la dimensión vertical. Por ello, el propósito de este estudio es evaluar los métodos más utilizados y confiables para la determinación del plano oclusal, mediante una revisión de la literatura científica actual. A partir de lo investigado, se concluye que el plano oclusal debe ubicarse en la posición que ocupaban los dientes naturales, y su determinación incluye una secuencia clínica, que se inicia por el sector anterior en reposo y sonrisa, y continúa con el sector posterior. No existeun método absoluto. Es importante el análisis individual de cada paciente para decidir qué métodosserán los más indicados. Existen métodos que icluyen el análisis cefalométrico o tridimensional, lo que aporta una mayor precisión en la planificación.
Objetivo: Comparar la microdureza superficial de discos de acrílico de autocurado y termocurado en distintos periodos de tiempo. Metodología: Este estudio experimental, un ensayo en laboratorio in vitro, incluyó 80 discos de acrílico (Vitalloy), 40 de autocurado (A) y 40 de termocurado (T) divididos en 8 subgrupos: grupo control de autocurado GA0 (n = 10), grupo control de termocurado GT0 (n = 10), grupo de autocurado almancenado 1 día GA1 (n = 10), grupo de termocurado almacenado 1 día GT1 (n = 10), grupo de autocurado almacenado 7 días GA7 (n = 10), grupo de termocurado almacenado 7 días GT7 (n = 10), grupo de autocurado almacenado 21 días GA21 (n = 10), grupo de termocurado almacenado 21 días GT21 (n = 10); luego se evaluó la microdureza superficial Vickers de los discos de resina acrílica previamente almacenados en suero fisiológico en los distintos periodos de tiempo. Posteriormente, los datos fueron analizados estadísticamente mediante test de Anova y Tukey. El nivel de significancia estadística se tomó como p < 0,05. Resultados: Los valores encontrados fueron en el GT0 (20,45 ± 0,93 VHN); GA0 (16,25 ± 0,79 VHN); GT1 (20,08 ± 0,66 VHN); GA1 (15,97 ± 0,78 VHN); GT7 (19,57 ± 1,54 VHN); GA7 (14,33 ± 0,48 VHN); GT21 (19,17 ± 1,26 VHN); GA21 (14,64 ± 0,52 VHN), presentando diferencias estadísticamente significativas ambos grupos autocurado y termocurado (p < 0,001). Conclusión: Los grupos de resinas acrílicas de termocurado presentaron mejores valores de microdureza que los grupos de resinas acrílicas de autocurado en los distintos periodos de tiempo evaluados.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.