Ionic transport behaviors of silver chloride (AgCl) have been revealed with impedance spectra measurement under high pressures up to 20.4 GPa. AgCl always presented ionic conducting under experimental pressures, but electronic conduction can coexist with ionic conduction within the pressure range from 6.7 to 9.3 GPa. The ionic conductivity of AgCl decreases by three orders of magnitude under compression, indicating that Ag+ ion migrations are suppressed by high pressure. A parameter, fW, was defined as the starting frequency at which Ag+ ions begin to show obvious long-distance diffusion in AgCl. fW showed a similar trend with the ionic conductivity under high pressures, indicating that the speed of Ag+ ion diffusion slows down as the pressure increases. Unlike AgI, Ag+ ion diffusion in AgCl is controlled by the indirect-interstitial mechanism. Due to stronger ionic bonds and larger lattice deformation, Ag+ ion diffusion in the rigid Cl− lattice is more difficult than in the I− lattice under high pressures.

The electrical transport and structural properties of tin oxide nanoparticles under compression have been studied by in situ impedance measurements and synchrotron X-ray diffraction (XRD) up to 27.9 GPa. It was found that the conduction of SnO2 can be improved significantly with compression. Abnormal variations in resistivity, relaxation frequency, and relative permittivity were observed at approximately 12.3 and 25.0 GPa, which can be attributed to pressure-induced tetragonal- orthorhombic-cubic structural transitions. The dielectric properties of the SnO2 nanoparticles were found to be a function of pressure, and the dielectric response was dependent on frequency and pressure. The dielectric constant and loss tangent decreased with increasing frequency. Relaxation-type dielectric behaviour dominated at low frequencies. Whereas, modulus spectra indicated that charge carrier short-range motion dominated at high frequencies.