This paper concerns an international research project aimed at determining the Avogadro constant by counting the atoms in an isotopically enriched silicon crystal. The counting procedure was based on the measurement of the molar volume and the volume of an atom in two 1 kg crystal spheres. The novelty was the use of isotope dilution mass spectrometry as a new and very accurate method for the determination of the molar mass of enriched silicon. Because of an unexpected metallic contamination of the sphere surfaces, the relative measurement uncertainty, 3 × 10−8 NA, is larger by a factor 1.5 than that targeted. The measured value of the Avogadro constant, NA = 6.022 140 82(18) × 1023 mol−1, is the most accurate input datum for the kilogram redefinition and differs by 16 × 10−8 NA from the CODATA 2006 adjusted value. This value is midway between the NIST and NPL watt-balance values.

New results are reported from an ongoing international research effort to accurately determine the Avogadro constant by counting the atoms in an isotopically enriched silicon crystal. The surfaces of two 28 Si-enriched spheres were decontaminated and reworked in order to produce an outer surface without metal contamination and improved sphericity. New measurements were then made on these two reconditioned spheres using improved methods and apparatuses. When combined with other recently refined parameter measurements, the Avogadro constant derived from these new results has a value of N A = 6.022 140 76(12) × 10 23 mol -1 . The X-ray crystal density method has thus achieved the target relative standard uncertainty of 2.0 × 10 -8 necessary for the realization of the definition of the new kilogram.

The Avogadro constant links the atomic and the macroscopic properties of matter. Since the molar Planck constant is well known via the measurement of the Rydberg constant, it is also closely related to the Planck constant. In addition, its accurate determination is of paramount importance for a definition of the kilogram in terms of a fundamental constant. We describe a new approach for its determination by counting the atoms in 1 kg single-crystal spheres, which are highly enriched with the 28Si isotope. It enabled isotope dilution mass spectroscopy to determine the molar mass of the silicon crystal with unprecedented accuracy. The value obtained, NA = 6.022,140,78(18) × 10(23) mol(-1), is the most accurate input datum for a new definition of the kilogram.

A new single crystal from isotopically enriched silicon was used to determine the Avogadro constant N A by the x-ray-crystal density method. The new crystal, named Si28-23Pr11, has a higher enrichment than the former 'AVO28' crystal allowing a smaller uncertainty of the molar mass determination. Again, two 1 kg spheres were manufactured from this crystal. The crystal and the spheres were measured with improved and new methods. One sphere, Si28kg01a, was measured at NMIJ and PTB with very consistent results. The other sphere, Si28kg01b, was measured only at PTB and yielded nearly the same Avogadro constant value. The mean result for both 1 kg spheres is N A = 6.022 140 526(70) × 10 23 mol −1 with a relative standard uncertainty of 1.2 × 10 −8 . This value deviates from the Avogadro value published in 2015 for the AVO28 crystal by about 3.9(2.1) × 10 −8 . Possible reasons for this difference are discussed and additional measurements are proposed.

We measured the absolute lengths of three single crystal silicon samples by means of an imaging Twyman-Green interferometer in the temperature range from 7 K to 293 K with uncertainties of about 1 nm. From these measurements we extract the coefficient of thermal expansion with uncertainties in the order of 1 × 10 −9 /K. To access the functional dependence of the length on the temperature usually polynomials are fitted to the data. Instead we use a physically motivated model equation with 7 fit parameters for the whole temperature range. The coefficient of thermal expansion is obtained from the derivative of the best fit. The measurements conducted in 2012 and 2014 demonstrate a high reproducibility and the agreement of two independently produced samples supports single crystal silicon as reference material for thermal expansion. Although the results for all three samples agree with each other and with measurements performed at other institutes, they significantly differ from the recommended values for thermal expansion of crystalline silicon.