By means of optical microscope, SEM and EDS, the microstructure of laser cladding layer under 1200W laser heat input was analyzed. Through the research, the relationship between precipitate characteristics and properties of the cladding layer was studied, and failure reason was found. The results show that Co, Cr and W elements have the tendency of short-range diffusion in the surface region in Stellite 6 alloy with a jagged shape. In this area, Co-Cr-W-Fe precipitated and hardened layer formed with high hardness and abrasive resistance but a lower ductility. Meanwhile, intergranular phase M23C6 precipitated. Some parts the big temperature gradient and overheat accelerated the precipitation process, led to the incomplete fusion of dendritic crystal, crack initiation and propagation on account of the integrated factors. Some solutions were put forward to reduce the failure risk.
As one of the widely used materials for hydro turbine runners, 13Cr4Ni martensitic stainless steels (13/4 MSS) manufactured by forging and wire arc additive manufacturing (WAAM), respectively, were selected for high-cycle fatigue tests, and the effects of microstructures and defect characteristics on fatigue mechanism were investigated. The results indicate that compared to the forged 13/4 MSS, the microstructure of the WAAM test piece is very fine, and the martensite units, consequently, are smaller in size. The yield strength and ultimate tensile strength are 685 MPa and 823 MPa for the forged specimen and 850 MPa and 927 MPa for the WAAM specimens, respectively. The fatigue strength of 107 cycles at room temperature is 370 MPa for forged specimens and 468 MPa for WAAM specimens. The predominant defect of the forged 13/4 MSS specimen is inclusion, and the fatigue initiates mainly at the surface and subsurface. While for the WAAM specimen, the most commonly found defects are pores, and the fatigue initiation is internal and at the subsurface. In addition, the fine microstructure, as well as the high strength and hardness, enable the WAAM material to have higher fatigue strength. In order to assess the effect of defects on fatigue performance, the stress intensity factor and El-Haddad model were adopted in the present study. It was found that the forged specimens with fish-eye (FIE) zones and the WAAM specimens with granular bright facet (GBF) zones have longer fatigue life. The fatigue strengths of the forged 13/4 MSS were therefore predicted by defect size. In contrast, the fatigue strengths of the WAAM 13/4 MSS were predicted by both defect and GBF sizes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.