The bonding technique that incorporated dentin removal from the fragment before bonding showed greater fracture strength across all groups. Fragment dehydration for 48 h caused a reduction in fracture strength, which was recovered by a 30-min rehydration.
The purpose of this in vitro study was to evaluate alterations in the surface roughness and micromorphology of human enamel submitted to three prophylaxis methods. Sixty-nine caries-free molars with exposed labial surfaces were divided into three groups. Group I was treated with a rotary instrument set at a low speed, rubber cup and a mixture of water and pumice; group II with a rotary instrument set at a low speed, rubber cup and prophylaxis paste Herjos-F (Vigodent S/A Indústria e Comércio, Rio de Janeiro, Brazil); and group III with sodium bicarbonate spray Profi II Ceramic (Dabi Atlante Indústrias Médico Odontológicas Ltda, Ribeirão Preto, Brazil). All procedures were performed by the same operator for 10 s, and samples were rinsed and stored in distilled water. Pre and post-treatment surface evaluation was completed using a surface profilometer (Perthometer S8P, Marh, Perthen, Germany) in 54 samples. In addition, the other samples were coated with gold and examined in a scanning electron microscope (SEM). The results of this study were statistically analyzed with the paired t-test (Student), the Kruskal-Wallis test and the Dunn (5%) test. The sodium bicarbonate spray led to significantly rougher surfaces than the pumice paste. The use of prophylaxis paste showed no statistically significant difference when compared with the other methods. Based on SEM analysis, the sodium bicarbonate spray presented an irregular surface with granular material and erosions. Based on this study, it can be concluded that there was an increased enamel surface roughness when teeth were treated with sodium bicarbonate spray when compared with teeth treated with pumice paste.
The purpose of this study was to test the hypothesis that both human and bovine sclerotic dentin have similar hardness properties, in addition to similar micromorphological characteristics. Sixteen teeth (8 human and 8 bovine) exhibiting exposed dentin in the incisal edge and showing characteristics typical of sclerosis were used. Vickers surface microhardness testing was conducted. Three areas of the dentin surface of each specimen were selected. All teeth were processed for scanning electron microscopy in order to estimate the amount (in percentage) of solid dentin on the sclerotic dentin surface. The data were compared by Student's t test (α = 0.05). The micromorphological and microhardness data were compared by Pearson's linear correlation test (α = 0.05). The mean percentages of solid dentin of human and bovine sclerotic dentin were similar (human 90.71 ± 0.83 and bovine 89.08 ± 0.81, p = 0.18). The mean microhardness value (VHN) of human sclerotic dentin was significantly higher than that of bovine sclerotic dentin (human 45.26 ± 2.92 and bovine 29.93 ± 3.83, p = 0.006). No correlation was found between the microhardness values and the amount of solid dentin in the sclerotic dentin, irrespective of the species considered (human R 2 = 0.0240, p = 0.714; bovine R 2 = 0.0017, p = 0.923; and combined R 2 = 0.038, p = 0.46). We concluded that although both bovine and human sclerotic dentin present a similar amount of solid tissue, human sclerotic dentin presents higher microhardness than bovine sclerotic dentin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.