In this research work, an attempt was made to machine Ti6Al4V titanium alloy utilizing AA6061/10Gr composite tool. The composite tool was fabricated using stir casting technique and Al2O3 particles of size 5µm were incorporated in the dielectric fluid to enhance the machining performance. Experiments were conducted by varying Al203 concentration, pulse on time, current, and pulse off time, and the responses Material Removal Rate (MRR), Tool Wear Rate (TWR), and Surface Roughness (Ra) were recorded. Experiments runs were planned using Taguchi orthogonal array. The results revealed that adding powder increases MRR and TWR owing to the excessive heat generation and bridging effect respectively. The best surface finish was attained due to the increase in spark gap and complete flushing of machined debris. Coating of materials over the machined specimen was observed when the parametric value of Ton was higher than 60s under PMEDM conditions. Pits, craters and cracks were observed on the machined topography which was eliminated when 5g/l of Al2O3 particles were added to dielectric fluid. MEIOT technique was utilized for optimization and it was observed that Ton 15µs, Toff 4µs and current 7A and powder concentration of 10g/l results in best machining performance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.