Objectives: To investigate and compare the characteristics of commonly used types of traditional and heat-activated initial archwires at different temperatures by plotting their load/deflection graphs and quantifying three parameters describing the discharge plateau phase. Materials and Methods: Forty-eight archwires of cross-sectional diameters ranging from 0.010 inches to 0.016 inches were obtained from seven different manufacturers. A modified three-point wire-bending test was performed on three analogous samples of each type of archwire at 55uC and 5uC, simulating an inserted archwire that is subjected to cold or hot drinks during a meal. For each resulting load/deflection curve the plateau section was isolated and the mean value of each parameter for each type of wire was obtained. Results: Permanent strain was exhibited by all wires tested at 55uC. Statistically significant differences were found between almost all wires for the three considered parameters when tested at 55uC and 5uC. Loads were greater at 55uC than at 5uC. Differences were also found between traditional and heat-activated archwires, the latter of which generated longer plateaus at 55uC, shorter plateaus at 5uC, and lighter mean forces at both temperatures. The increase in average force seen with increasing diameter tended to be rather stable at both temperatures. Conclusions: All nickel-titanium wires tested showed a significant change related to temperature in terms of behavior and force for both traditional and heat-activated wires. Stress under high temperatures can induce permanent strain, whereas the residual strain detected at low temperatures can be recovered from as temperature increases. (Angle Orthod. 2013;83:298-305.)

ObjectivesThe aim of this study is to investigate and compare the characteristics of as received and retrieved NiTi archwires at a constant temperature by plotting their load/deflection graphs and quantifying three parameters describing the discharge plateau phase.Materials and methodsTwo hundred four NiTi archwires, traditional and heat-activated, of various cross sections, were obtained from 5 different manufacturers. Specimens prepared from the selected wires were subjected to a three-point bending test where 92 were retrieved through an in vivo retrieval protocol (crowding group C1 and group C2), 56 went through an in vitro retrieval protocol, and 56 were as received. The in vitro retrieval protocol was performed by a gear motor connected to a stainless steel support that performed fatigue cycles to the bent wires in artificial saliva. The load/deflection graphs of as received and retrieved wires were described through three parameters and the results were analyzed with classification and regression trees (CART) and analysis of variance (ANOVA).ResultsStatistically significant differences between as received and retrieved wires were found only for the parameter plateau slope which represents the constancy of force expressed by the wire.ConclusionsThe aging of NiTi archwires influences the force constancy expressed. The behavior of the wires changes depending on the size, brand, and type of retrieval protocol. In terms of performance, the poorest is represented by all wires retrieved in vitro and in vivo group C2 (moderate to severe crowding).