To understand functional roles of constituent elements in ternary metal oxide photoanodes, essential photoelectrochemical (PEC) properties are systematically analyzed on a series of copper vanadate compounds with different Cu:V elemental ratios. Homogeneous and highly continuous thin films of β-CuVO, γ-CuVO, CuVO, and CuVO are grown via reactive co-sputtering and their performance characteristics for the light-driven oxygen evolution reaction are evaluated. All four compounds have similar bandgaps in the range of 1.83-2.03 eV, though Cu-rich phases exhibit stronger optical absorption and higher charge separation efficiencies. Transient photocurrent analysis reveals a reduction of surface catalytic activity with increasing Cu:V elemental ratio due to competitive charge recombination at Cu-related surface states. This comprehensive analysis of PEC functionalities-including photon absorption, carrier separation, and heterogeneous charge transfer-informs strategies for improving PEC activity in the copper vanadate materials system and provides insights that may aid discovery, design, and engineering of new photoelectrode materials.
The exploration of the synthetic space of halide perovskites hinges on an enormous number of parameters requiring time-consuming experimentation to decouple and optimize. Here, the formation of the prototype material CH 3 NH 3 PbI 3 (MAPbI 3 ) is investigated at different time and length scales using multimodal in situ measurements to monitor the evolution of crystalline phases, morphology, and photoluminescence as a function of the lead precursors. Kinetically fast formation of crystalline precursor phases already during the spin-coat deposition is observed using lead iodide (PbI 2 ) or lead chloride (PbCl 2 ) routes. These precursor phases most likely template final MAPbI 3 film morphology. In particular, the emergence of the "needle-like" structure is shown to appear before film annealing. In situ photoluminescence measurements suggest nanoscale nucleation followed by rapid nuclei densification and growth. Using this multimodal in situ approach, different formation pathways can be identified either via precursor phases in the PbI 2 and PbCl 2 routes or direct perovskite formation from molecular building blocks as observed in the lead acetate (PbAc 2 ) route. Correlation of in situ results with photovoltaic device performance demonstrates the power of in situ multimodal techniques, paves the way to a fast screening of synthetic parameters, and ultimately leads to controlled synthetic procedures that yield high-efficiency devices.
Cross-sections of a hole-conductor-free CH3NH3PbI3 perovskite solar cell were characterized with Kelvin probe force microscopy. A depletion region width of about 45 nm was determined from the measured potential profiles at the interface between CH3NH3PbI3 and nanocrystalline TiO2, whereas a negligible depletion was measured at the CH3NH3PbI3/Al2O3 interface. A complete solar cell can be realized with the CH3NH3PbI3 that functions both as light harvester and hole conductor in combination with a metal oxide. The band diagrams were estimated from the measured potential profile at the interfaces, and are critical findings for a better understanding and further improvement of perovskite based solar cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.