In this paper, a homogenous pure Barium Titanate with formula (BaTiO3) was prepared from pure Barium Carbonate (BaCO3) and titanium dioxide (TiO2) using the solid-state reaction technique, were used as raw materials having micro size by mixing of molar ratio [1:1], the powder was calcined at temperatures (900-1350) °C. The solid-State reaction can consider as an attractive process realistic alternative to the expensive wet-chemical route, according to X-ray diffraction, all of the peaks of Barium Titanate powder were perfectly suited to the positions of the peaks of the standard tetragonal phase in the pattern for this process. And with preferred crystalline size for the powder calcined at 1350 °C manifested the best results, where all the peaks indicate the formation of Barium Titanate completely. In addition, each BaTiO3 Nanopowder was compared to a micro powder that had been manufactured, by conducting x-ray diffraction, diffraction peaks undergo shifting toward higher angle to the high value of 2Ө, and Nano powder particles are smaller than micro powder particles. And this refers to a decrease in lattice parameters, in terms of the peaks of the Nano powder preceding the peaks of the micro powder of BaTiO3 and that match the result that is obtained by scanning electron microscopy (SEM).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.