Ti-6Al-4V (TA6V) titanium alloy is widely used in industrial applications such as aeronautic and aerospace due to its good mechanical properties at high temperatures. Experiments on two different resistive pulse heating devices (CEA Valduc and TU-Graz) have been carried out in order to study thermophysical properties (such as electrical resistivity, volume expansion, heat of fusion, heat capacity, normal spectral emissivity, thermal diffusivity, and thermal conductivity) of both solid and liquid Ti-6Al-4V. Fast timeresolved measurements of current, voltage, and surface radiation and shadowgraphs of the volume have been undertaken. At TU-Graz, a fast laser polarimeter has been used for determining the emissivity of liquid Ti-6Al-4V at 684.5 nm and a differential scanning calorimeter (DSC) for measuring the heat capacity of solid Ti-6Al-4V. This study deals with the specific behavior of the different solid phase transitions (effect of heating rate) and the melting region, and emphasizes the liquid state (T >2000 K).

Ohmic pulse-heating with sub-microsecond time resolution is used to obtain thermophysical properties for aluminum in the liquid phase. Measurement of current through the sample, voltage drop across the sample, surface radiation, and volume expansion allow the calculation of specific heat capacity and the temperature dependencies of electrical resistivity, enthalpy, and density of the sample at melting and in the liquid phase. Thermal conductivity and thermal diffusivity as a function of temperature are estimated from resistivity data using the Wiedemann-Franz law. Data for liquid aluminum obtained by pulse-heating are quite rare because of the low melting temperature of aluminum with 933.47 K (660.32°C), as the fast operating pyrometers used for the pulse-heating technique with rise times of about 100 ns generally might not be able to resolve the melting plateau of aluminum because they are not sensitive enough for such low temperature ranges. To overcome this obstacle, we constructed a new, fast pyrometer sensitive in this temperature region. Electromagnetic levitation, as the second experimental approach used, delivers data for surface tension (this quantity is not available by means of the pulse-heating technique) and for density of aluminum as a function of temperature. Data obtained will be extensively compared to existing literature data.

Enthalpy, resistivity, density, specific heat capacity, and normal spectral emissivity as a function of temperature of Inconel 718 alloy were measured by a fast resistive pulse heating technique up into the liquid phase, thus obtaining data on thermal conductivity and thermal diffusivity. The high‐speed measurements are compared with results of quasistatic measurements of specific heat obtained by differential‐scanning calorimetry and expansion measurements by dilatometry.

Wire-shaped iron samples are resistively volume heated as part of a fast capacitor discharge apparatus. Measurements of current through the specimen, voltage across the specimen, radiance temperature, and thermal expansion of the specimen as functions of time allow the determination of specific heat and various dependencies among enthalpy, electrical resistivity, temperature, and density for liquid iron up to 5000 K. High pressures, up to 3800 bar. are used to obtain the liquid state far above the normal boiling point. An estimate of critical-point data for iron is given by using experimental data of the vapor pressure of liquid iron.