The variation in the green intensity ratio ((2)H(11/2) and (4)S(3/2) energy levels to the ground state) of Er ions in silica fibers has been studied as a function of temperature. The different processes that are used to determine the population of these levels are investigated, in particular 800-nm excited-state absorption in Er-doped fibers and 980-nm energy transfer, in Yb-Er-codoped fibers. The invariance of the intensity ratio at a fixed temperature with respect to power, wavelength, and doped fiber length has been investigated and shown to permit the realization of a high-dynamic-range (greater than 600 °C), autocalibrated fiber-optic temperature sensor.

Conception, realization and characterization of a very high negative chromatic dispersion fiber. Optical Fiber Technology, Elsevier, 2002, 8, pp.89-105. hal-00469705

The spectroscopic properties of Tm(3+)/Yb(3+) co-doped silica fibers under excitation at 980 nm are reported. Three distinct up-conversion fluorescence bands were observed in the visible to near infra-red regions. The blue and red fluorescence bands at 475 and 650 nm, respectively, were found to originate from the (1)G(4) level of Tm(3+). A three step up-conversion process was established as the populating mechanism for these fluorescence bands. The fluorescence band at 800 nm was found to originate from two possible transitions in Tm(3+); one being the transition from the (3)H(4) to (3)H(6) manifold which was found to dominate at low pump powers; the other being the transition from the (1)G(4) to (3)H(6) level which dominates at higher pump powers. The fluorescence lifetime of the (3)H(4) and (3)F(4) levels of Tm(3+) and (2)F(5/2) level of Yb(3+) were studied as a function of Yb(3+) concentration, with no significant energy back transfer from Tm(3+) to Yb(3+) observed.

No abstract