The objective of this review was to analyze the process of wear of implants leading to the shedding of titanium particles into the peri-implant hard and soft tissues. Titanium is considered highly biocompatible with low corrosion and toxicity, but recent studies indicate that this understanding may be misleading as the properties of the material change drastically when titanium nanoparticles (NPs) are shed from implant surfaces. These NPs are immunogenic and are associated with a macrophage-mediated inflammatory response by the host. The literature discussed in this review indicates that titanium NPs may be shed from implant surfaces at the time of implant placement, under loading conditions, and during implant maintenance procedures. We also discuss the significance of the micro-gap at the implant-abutment interface and the effect of size of the titanium particles on their toxicology. These findings are significant as the titanium particles can have adverse effects on local soft and hard tissues surrounding implants, implant health and prognosis, and even the health of systemic tissues and organs.
Titanium wear is a growing area of interest within dental implantology. This study aimed to investigate titanium and zirconium wear from dental implants at the time of insertion using X-ray-fluorescence spectrometry (XRF) and an in vitro protocol utilizing artificial bovine bone plates. Five groups were analyzed using XRF-spectrometry: groups 1–4 (titanium implants) and group 5 (zirconia implants). The implants were inserted into two bone blocks held together by a vice. The blocks were separated, and the insertion sites were analyzed for titanium (Ti) and zirconium (Zr). Statistical descriptive analyses of Ti and Zr concentrations in the coronal, middle and apical bone interface were performed. A comparative analysis confirmed differences between the implant’s surface stability and Ti accumulation within the insertion sites of the bone block. There was a direct relationship between implant length and the quantity of titanium found on the bone block. The data generally indicates greater quantities of titanium in the coronal thirds of the implants, and less in the apical thirds. The titanium and zirconium found in the bone samples where the group 5 implants were inserted was not of statistical significance when compared to control osteotomies. The results of this study confirm wear from metallic, but not ceramic, dental implants at the time of insertion.
Denture teeth are used for removable prostheses and implant-supportive restorations. The purpose of this study was to analyze the surface of artificial teeth following exposure to different liquids. Mechanical wear and the cleaning of artificial teeth were also investigated. Two groups of resin teeth were used; original surface (Group A) and surface abrasion/wear (Group B). The teeth were exposed for 24 h to water (control), cola (Group 1), coffee (Group 2), tea (Group 3), chlorhexidine (Group 4), and red wine (Group 5). Baseline measurements of liquids were taken. An x-ray fluorescence spectrometric analysis was performed. Data were evaluated using semi-quantitative descriptive analysis. The data showed approximate increases of peak intensity for Group A1-2-fold Fe, 2-fold Ni, 2.2-fold Zn; for Groups A2 and A3- less than 1.5-fold Fe, Ni, and Zn. Group B yielded similar results; however, the increases in Fe, Ni, and Zn were significantly higher in Groups 1 and 2 (ranged 2-4-fold increases in intensity). Group B3 showed little increase in Fe, Ni, and Zn. Groups A4 and A5 showed intensity increases for Zn. Groups A1–A5 showed reductions in intensity following 30 s of cleaning. A pronounced accumulation of iron, nickel, and zinc was found after exposure to liquids, especially when artificial teeth were worn down. Peak intensities were reduced following 30 s of brushing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.