The tadpole‐shaped amphiphilic copolymers with cyclic polystyrene as the head and a linear poly(N‐isopropylacrylamide) as the tail have been successfully synthesized by combination of reversible addition‐fragmentation chain transfer (RAFT) polymerization and “click” reaction. The synthesis involves two main steps: (1) preparation of a linear acetylene‐terminated PNIPAAM‐b‐PS with a side azido group anchored at the junction between two blocks; (2) intramolecular cyclization reaction to produce the cyclic PS block using “click” chemistry under high dilution. The structures, molecular weights, and molecular weight distributions of the resulted intermediates and the target polymers were characterized by their 1H NMR, FTIR, and gel permeation chromatography. The difference of surface property between tadpole‐shaped polymer and its linear precursor was observed, and the water contact angles on the former surface are larger than that of the latter surface. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2390–2401, 2008

Well‐defined figure‐of‐eight‐shaped (8‐shaped) polystyrene (PS) with controlled molecular weight and narrow polydispersities has been prepared by the combination of atom transfer radical polymerization (ATRP) and click chemistry. The synthesis involves two steps: 1) Preparation of a linear tetrafunctional PS with two azido groups, one at each end of the polymer chain, and two acetylene groups at the middle of the chain. 2) Intramolecular cyclization of the linear tetrafunctional PS at a very low concentration by a click reaction to produce the 8‐shaped polystyrenes. The resulting intermediates and the target polymers were characterized by 1H NMR and FT‐IR spectroscopy, and gel permeation chromatography. The glass transition temperatures (Tgs) were determined by differential scanning calorimetry and it was found that the decrease in chain mobility by cyclization resulted in higher Tgs for 8‐shaped polystyrenes as compared to their corresponding precursors.

The ABCD 4‐miktoarm star polymers based on polystyrene (PS), poly(ε‐caprolactone) (PCL), poly(methyl acrylate) (PMA), and poly(ethylene oxide) (PEO) were synthesized and characterized successfully. Using the mechanism transformation strategy, PS with three different functional groups (i.e., hydroxyl, alkyne, and trithiocarbonate), PS‐HEPPA‐SC(S)SC12H25, was synthesized by the reaction of the trithiocarbonate‐terminated PS with 2‐hydroxyethyl‐3‐(4‐(prop‐2‐ynyloxy)phenyl) acrylate (HEPPA) in tetrahydrofuran (THF) solution. Subsequently, the ring‐opening polymerization (ROP) of ε‐caprolactone (CL) was carried out in the presence of stannous(II) 2‐ethylhexanoate and PS‐HEPPA‐SC(S)SC12H25, and then the PS‐HEPPA(PCL)‐SC(S)SC12H25 obtained was used in reversible addition‐fragmentation chain transfer (RAFT) polymerization of methyl acrylate (MA) to produce the ABC 3‐miktoarm star polymer, S(PS)(PCL)(PMA) carrying an alkyne group. The ABCD 4‐miktoarm star polymer, S(PS)(PCL)(PMA)(PEO) was successfully prepared by click reaction of the alkyne group on the HEPPA unit with azide‐terminated PEO (PEO‐N3). The target polymer and intermediates were characterized by NMR, FTIR, GPC, and DSC. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 6641–6653, 2008

Well‐defined hetero eight‐shaped copolymers composed of polystyrene (PS) and poly(ε‐caprolactone) (PCL) with controlled molecular weight and narrow molecular weight distribution were successfully synthesized by the combination of ring‐opening polymerization, ATRP, and “click” reaction. The synthetic procedure involves three steps: (1) preparation of a tetrafunctional PS and PCL star copolymer with two PS and two PCL arms using the tetrafunctional initiator bearing two hydroxyl groups and two bromo groups; (2) synthesis of tetrafunctional star copolymer, (α‐acetylene‐PCL)2(ω‐azido‐PS)2, by the transition of terminal hydroxyl and bromo groups to acetylene and azido groups through the reaction with 4‐propargyloxybutanedioyl chloride and NaN3 respectively; (3) intramolecular cyclization reaction to produce the hetero eight‐shaped copolymers using “click” chemistry under high dilution. The 1H NMR, FTIR, and gel permeation chromatography techniques were applied to characterize the chemical structures of the resulted intermediates and the target polymers. Their thermal behavior was investigated by DSC, and their crystallization behaviors of PCL were studied by polarized optical microscopy. The decrease in chain mobility of the eight‐shaped copolymers restricts the crystallization of PCL and the crystallization rate of PCL is slower in comparison with their corresponding star precursors. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 6496–6508, 2008

No abstract