The effects of frequency in the range 20 to 60 kHz, acoustic power and horn to specimen distance on the corrosion of 304L stainless steel in an ultrasonic field were investigated. At 40 and 60 kHz, the corrosion rate increased to a maximum and thereafter decreased with increasing transmitted power. At 20 kHz, the corrosion rate increased continuously with increasing power over the range investigated. At 18 W transmitted power, the corrosion rate increased continuously with frequency. However, at 40 W transmitted power a pronounced maximum in the corrosion rate occurred at 40 kHz. A significant effect of horn to specimen distance was found, the corrosion rate increasing with decreasing distance. High corrosion rates in excess of 800 mm yr(-1) were observed when the specimen was situated 0.1 mm from the radiating face of the ultrasonic probe. In addition, the area affected by sonication was found to increase with increasing distance.
A systematic study of the effect exerted by various parameters on the corrosion of 304L stainless steel in an ultrasonic field has been carried out. Ultrasound increased the corrosion rate under all the investigated conditions. In this paper, attention is focused on the effect of temperature and hydrostatic pressure. At ambient pressure, increase in temperature, T, was found to increase the ultrasonically enhanced corrosion rate up to a maximum of 40 degrees C; at 50 degrees C a marked decrease in the effect of ultrasound was observed. At constant temperature, increase in hydrostatic pressure caused a strong increase in corrosion rate to values in excess of 2500 mm yr(-1) at 4 bar.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.