The ‘‘hyperfine magnetic field’’- Hhpf at the nuclei of the diamagnetic atoms 119Sn was measured in Heusler alloy Ni2MnSn by Mössbauer absorption spectroscopy for pressures up to 10.8 GPa at room temperature. The pressure dependences of HhpfSn does not show hysteresis and can be fitted by a linear function HhpfSn(P)/HhpfSn(0) =1+kH⋅P with the coefficient kH=−0.095±0.015 GPa−1, where HhpfSn(0)=4.60±0.12T. Diamond anvil cells were used to obtain high pressure at room temperature. The Curie temperature (TC) has been measured (up to 5.2 GPa) in the ‘‘toroid’’ high pressure device using thermal ac susceptibility measurements. That pressure dependence was linear with the coefficient dTC/dP=7.44 K/Gpa [TC(0)=341.3 K]. The compressibility of the sample has been measured by means of resistive strain gauges at hydrostatic pressure up to 9 GPa. The equation (V−V0)/V0=−a⋅P+b⋅P2 has been fitted to the experimental data with the coefficients a=8.64⋅10−3 GPa−1, b=1.13⋅10−4 GPa−2. The drop of the HhpfSn in pressure range 0–10.8 GPa can be explained on the basis of the empirical theory developed by Delyagin, Krylov, and Nesterov [JETP 76, 1049(1980)].
This is an Accepted Manuscript of an article published by Taylor & Francis in Materials Science and Technology on 17 March 2017, available online: http://www.tandfonline.com/doi/full/10.1080/02670836.2017.1302141. Under embargo. Embargo end date: 17 March 2018.Results of corrosion tests of titanium in the initial state and after treatment using pulsed magnetic field are presented. It is shown that samples after treatment have better corrosion resistance due to the formation of denser and finer corrosion products with better adhesion to the substrate. Samples after treatment have more homogeneous microstructure due to a substantial increase of dislocations which are uniformly distributed. Mechanisms of dislocation multiplication and a model explaining the effect of the treatment on the corrosion are discussed
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.