A new single-crystal diffraction facility has been constructed on beamline 9 of the SRS at Daresbury Laboratory for the study of structural problems in chemistry and materials science. The station utilizes up to 3.8 mrad horizontally from the 5 T wiggler magnet which can be focused horizontally and vertically. The horizontal focusing is provided by a choice of gallium-cooled triangular bent Si (111) or Si (220) monochromators, giving a wavelength range from 0.3 to 1.5 A. Focusing in the vertical plane is achieved by a cylindrically bent zerodur mirror with a 300 mum-thick palladium coating. The station is equipped with a modified Enraf-Nonius CAD-4 four-circle diffractometer and a Siemens SMART CCD area-detector system. High- and low-temperature facilities are available to cover the temperature range from about 80 to 1000 K. Early results on test compounds without optimization of the beam optics demonstrate that excellent refined structures can be obtained from samples giving diffraction patterns too weak to be measured with conventional laboratory X-ray sources, fulfilling a major objective of the project.
The version in the Kent Academic Repository may differ from the final published version. Users are advised to check http://kar.kent.ac.uk for the status of the paper. Users should always cite the published version of record.
Ahstnet X-ray diffraction panems of equimolecular concentrated aqueous solutions of yttrium chloride and bromide have been investigated from s = 0.4 A-' up to s = 15 .&-I, An assumed coordination of eight water molecules around each ymium cation, at a distauce of 2.36 A. reproduces the intensity at high s values in agreement with the values obtained by some of the present authors from WAFS experiments. Narrow interference maxima at s = (4n sin0)jX E 0.9 A-' may be interpreted as the existence of a local order of the hydrated yttrium cations surrounded by anions and free water molecules. Structural models with and without close packing of lhe hydrated cations were built to simulate fhat local order.
A new beamline (MPW6.2) has been designed and built for the study of materials during processing where three synchrotron techniques, SAXS, WAXS and XAS, are available simultaneously. It has been demonstrated that Rietveld refinable data can be collected from silicon SRM 640b over a 60 degrees range in a time scale of 1 s. The data have been refined to a chi(2) of 2.4, the peaks fitting best to a Pearson VII function or with fundamental parameters. The peak halfwidths have been found to be approximately constant at 0.06 degrees over a 120 degrees angular range indicating that the instrumental resolution function has matched its design specification. A quantitative comparison of data sets collected on the same isotactic polypropylene system on MPW6.2 and DUBBLE at the ESRF shows a 17% improvement in angular resolution and a 1.8 improvement in peak-to-background ratio with the RAPID2 system; the ESRF data vary more smoothly across detector channels. The time-dependent wide-angle XRD was tested by comparing a hydration reaction of gypsum-bassanite-anhydrite with energy-dispersive data collected on the same system on the same time scale. Three sample data sets from the reaction were selected for analysis and gave an average chi(2) of 3.8. The Rietveld-refined lattice parameters are a good match with published values and the corresponding errors show a mean value of 3.3 x 10(-4). The data have also been analysed by the Pawley decomposition phase-modelling technique demonstrating the ability of the station to quickly and accurately identify new phases. The combined SAXS/WAXS capability of the station was tested with the crystallization and spinodal decomposition of a very dilute polymer system. Our measurements show that the crystallization of a high-density co-polymer (E76B38) as low as 0.5% by weight can be observed in solution in hexane. The WAXS and SAXS data sets were collected on the same time scale. The SAXS detector was calibrated using a collagen sample that gave 30 orders of diffraction in 1 s of data collection. The combined XRD and XAS measurement capability of the station was tested by observing the collapse and re-crystallization of zinc-exchanged zeolite A (zeolite Zn/Na-A). Previous studies of this material on station 9.3 at the SRS were compared with those from the new station. A time improvement of 38 was observed with better quality counting statistics. The improved angular resolution from the WAXS detector enabled new peaks to be identified.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.