Elastic properties of the heavy fermion superconductor URu2Si2Wolf, B.; Sixl, W.; Graf, R.; Finsterbusch, D.; Bruls, G.; Luthi, B.; Knetsch, E.A.; Menovsky, A.A.; Mydosh, J.A.
General rightsIt is not permitted to download or to forward/distribute the text or part of it without the consent of the author(s) and/or copyright holder(s), other than for strictly personal, individual use, unless the work is under an open content license (like Creative Commons).
Disclaimer/Complaints regulationsIf you believe that digital publication of certain material infringes any of your rights or (privacy) interests, please let the Library know, stating your reasons. In case of a legitimate complaint, the Library will make the material inaccessible and/or remove it from the website. Please Ask the Library: http://uba.uva.nl/en/contact, or a letter to: Library of the University of Amsterdam, Secretariat, Singel 425, 1012 WP Amsterdam, The Netherlands. You will be contacted as soon as possible.
Download date: 08 May 2018Journal of Low Temperature Physics, Vol. 94, Nos. 3/4, 1994
Ultrasonic measurements were performed on a fci Zn-Mg-Y quasicrystal and on the related parent compound Zn2Mg. Absolute values of both the longitudinal and the transverse sound velocities as well as their temperature dependence were determined. The temperature dependence of the quasicrystal sound velocity in the millikelvin temperature range is very similar to the logarithmic behaviour observed for amorphous materials.Introduction. -Since the discovery of the first quasicrystalline structure by Shechtman et al. [1] in 1984 in the system Al-Mn, there is a great interest in these long-range ordered but not periodic structures. However, only a few systems exist which are thermodynamically stable, most of them in the Al-TM system (TM = transition metal) like Al-Li-Cu [2], Al-Cu-Fe [3] and Al-Pd-Mn [4]. In 1993 a stable icosahedral phase was discovered in the system Zn-Mg-RE by Luo et al. [5]. This icosahedral phase turned out to be identical with the Z-phase found in 1982 by Padezhnova et al. [6] with a composition of Zn 6 Mg 3 Y 1 , whose structure could not be determined at that time. A detailed investigation showed the stability of the i-phase for the RE elements Y, Gd, Tb, Dy, Ho and Er [7]. In contrast to most of the other known i-phases, this system is based on Zn -not Al-as the main constituent. Another interesting feature of this quasicrystalline alloy is the possibility of incorporating RE elements with 4f -electron carrying a localized magnetic moment (Tb, Ho, Gd) in the quasicrystalline lattice.Since the determination of the primary solidification area in 1997 by Langsdorf et al. [8], large face-centred icosahedral (fci) Zn-Mg-RE single grains can be grown from the melt by different techniques [9][10][11]. Since then, measurements on single grains could be performed. Recent results of neutron scattering experiments show that the fci Zn-Mg-RE quasicrystals do not develop long-range magnetic order [12], however, diffuse-scattering data can be interpreted as short-range spin correlations in a six-dimensional hypercubic crystal [13]. So far, no ultrasonic investigations have been done in this system.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.