The article studied the effect of annealing on the structure and properties of zirconium dioxide coatings obtained by detonation spraying. Detonation spraying was realized on a computerized detonation spraying complex of the new generation CCDS2000. Determined that coatings made of zirconium dioxide are characterized by high adhesive strength of adherence to the substrate. Thermal annealing of coated samples was performed at temperatures of 900-1200◦ C. It was determined that the microhardness of zirconium dioxide coatings increases by 10-25% depending on the annealing temperature after annealing. The results of nanoindentation showed that the nanohardness of the coatings after annealing at 1000◦ C increases by 50%. It was determined that after annealing at 1000◦ C, the elastic modulus of the coatings increases, which indicates a decrease in plasticity and an increase in the strength of the coatings. X-ray diffraction analysis showed that the phase composition of coatings before and after annealing consists of t-ZrO2. After annealing occurs there is an increase in the degree of t-ZrO2 tetragonality. Electron microscopic analysis showed that an increase in the number and size of micro-continuity in the form of thin layers after annealing. Determined that increase the hardness of zirconium dioxide after annealing at 900-1200◦ C is associated with a higher degree of tetragonality t-ZrO2 phase.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.