Two new polymeric materials (polymers A and B) containing covalently bound iodine were prepared. These polymers were evaluated with respect to their possible use as radiopaque implant biomaterials--that is, materials that are visible in a noninvasive manner using routine X-ray absorption imaging techniques. Polymer A is a copolymer of methyl methacrylate (MMA) and 1 (80 and 20 mol%, respectively). Polymer B was prepared from MMA, 1, and 2-hydroxyethyl methacrylate (HEMA) (mol ratio 65:20:15, respectively). Compound 1 was synthesized from 4-iodophenol and methacryloyl chloride. The resulting polymers were characterized with GPC, DSC, NMR, and by measuring both the advancing and receding contact angles. Thrombogenicity of the polymers was determined by an in vitro thrombin generation test procedure. The maximum concentration of free thrombin was 76 +/- 1 nM for polymer A, and 64 +/- 3 nM for polymer B. The lag times (i.e., time onset of thrombin generation) were 392 seconds for polymer A and 553 seconds for polymer B. For PVC-T, which is known as a passive material, a lag time of 583 seconds was found. This indicates that polymer B is comparable to PVC-T, and more passive than polymer A. Polymer A exhibited minor activation of platelets. Polymer B did not induce platelet activation at all. The polymers exhibited, even as fibers with a diameter of ca. 0.3 mm, good radiopacity with routine imaging X-ray techniques in the clinic.(ABSTRACT TRUNCATED AT 250 WORDS)
A methacrylic monomer containing three iodine atoms, 2- [2',3',5'-triiodobenzoyl]-ethyl methacrylate (compound 1), was prepared in pure form. Compound 1 can be reacted with other methacrylates, such as methyl methacrylate (MMA), and 2-hydroxyethyl methacrylate (HEMA) with high conversion. Typically, less than 0.5% of free monomer is left after polymerization. For example, compound 1 was reacted with MMA and HEMA in the molar ratio 7:73:20, respectively. This yielded a terpolymer with Tg = 86 degrees C, Mw = 47,000 g/ mol and Mn = 22,800 g/mol. This material was characterized by various physicochemical techniques, including gel permeation chromatography, differential scanning calorimetry, thermogravimetric analysis, and nuclear magnetic resonance (NMR) spectroscopy (1H at 400 MHz, DMSO-d6 solution). In addition the material was found to exhibit low surface thrombogenicity in vitro and a low propensity to activate contacting blood platelets. Furthermore it was found that the terpolymer is markedly radiopaque: even thin objects (< 0.5 mm) could be easily visualized using X-ray fluoroscopic techniques as are routinely used in the clinic, e.g., during coronary angiography. The combined results obtained with the present terpolymer (particularly its in vitro hemocompatibility and its radiopacity) leads to the suggestion that this type of polymer could be used as cardiovascular biomaterials, for instance for the construction of a new type of endovascular stents. These would be expected to show improved biocompatibility if compared with metallic stents which are currently used, for instance in conjunction with percutaneous transluminal coronary angioplasty (PTCA). A stent prototype, constructed from the present radiopaque terpolymer, is shown and discussed briefly.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.