Cellulose II nanowhiskers (CNW-II) were produced by treatment of microcrystalline cellulose with sulfuric acid by both controlling the amount of H(2)SO(4) introduced and the time of addition during the hydrolysis process. The crystalline structure was confirmed by both XRD and (13)C CP-MAS NMR spectroscopy. When observed between crossed polarizers, the cellulose II suspension displayed flow birefringence and was stable for several months. The CNW-II nanowhiskers were significantly smaller than the cellulose I nanowhiskers (CNW-I) and had a rounded shape at the tip. The CNW-II average length and height were estimated by AFM to be 153 ± 66 and 4.2 ± 1.5 nm, respectively. An average width of 6.3 ± 1.7 nm was found by TEM, suggesting a ribbon-shape morphology for these whiskers. The average dimensions of the CNW-II elementary crystallites were estimated from the XRD data, using Scherrer's equation. A tentative cross-sectional geometry consistent with both XRD and NMR data was then proposed and compared with the geometry of the CNW-I nanowhiskers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.