A poly(urethane-acrylate) polymer (PUA) was synthesized, and a sufficiently high molecular weight starting from urethane-acrylate oligomer (UAO) was obtained. PUA was then loaded with two types of powdered ligno-cellulosic waste, namely from licorice root and palm leaf, in amounts of 1, 5 and 10%, and the obtained composites were chemically and mechanically characterized. FTIR analysis of final PUA synthesized used for the composite production confirmed the new bonds formed during the polymerization process. The degradation temperatures of the two types of waste used were in line with what observed in most common natural fibers with an onset at 270 °C for licorice waste, and at 290 °C for palm leaf one. The former was more abundant in cellulose (44% vs. 12% lignin), whilst the latter was richer in lignin (30% vs. 26% cellulose). In the composites, only a limited reduction of degradation temperature was observed for palm leaf waste addition and some dispersion issues are observed for licorice root, leading to fluctuating results. Tensile performance of the composites indicates some reduction with respect to the pure polymer in terms of tensile strength, though stabilizing between data with 5 and 10% filler. In contrast, Shore A hardness of both composites slightly increases with higher filler content, while in stiffness-driven applications licorice-based composites showed potential due to an increase up to 50% compared to neat PUA. In general terms, the fracture surfaces tend to become rougher with filler introduction, which indicates the need for optimizing interfacial adhesion.
Due to its excellent properties, poly(ethylene terephthalate) (PET) is one of the most produced and consumed polymers. Among plastics, it represents the main contributor to environmental pollution. Following the circular economy model, the chemical upcycling of PET reduces the amount of waste generated and transforms it into high-value products. The depolymerization of poly(ethylene terephthalate) into oligomers or monomers leads to forming a library of reactive molecules involved in different polymerization processes to obtain compounds with improved properties. Herein, several β-hydroxy amines were synthesized and used for the chemical recycling of water bottle waste by an environmental benefit aminolysis process to get very useful new terephthalamide diol monomers. The recycled diol monomers were subsequently exploited to synthesize poly(urethane acrylates) (PUAs) UV-curable coatings, and their chemical, thermal and mechanical characterizations were performed. The results show the great potential of the developed synthesis protocols to obtain PUAs with final properties that can be modulated to meet the requirements of different applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.