This paper investigates the rheological, mechanical and electrical properties of a Ethylene-Vinyl Acetate (EVA) polymer filled with 1, 3 and 5 wt.% multi-walled carbon nanotubes (MWCNTs). The melt flow and pressure-volume-Temperature (pvT) behaviors of the EVA/MWCNT composites were investigated using a high-pressure capillary rheometer, while the electro-mechanical response was investigated on injection-molded samples. Rheological experiments showed that the melt shear viscosity of the EVA/MWCNT composite is dependent on nanotube loading and, at high shear rates, the viscosity showed temperature-dependent shear thinning behavior with a flow index n < 0.35. The specific volume of the EVA/MWCNT composite decreased with increasing pressure and MWCNT wt.%. The transition temperature, corresponding to the pvT crystallization, increased linearly with increasing pressure, i.e., about 20 to 30 °C when cooling under pressure. The elastic modulus, tensile strength and stress at break increased with increasing MWCNT wt.%, whereas the strain at break decreased, suggesting the formation of MWCNT secondary agglomerates. The electrical conductivity of the EVA/MWCNT composite increased with increasing MWCNT wt.% and melt temperature, reaching ~10−2 S/m for the composite containing 5 wt.% MWCNTs. Using the statistical percolation theory, the percolation threshold was estimated at 0.9 wt.% and the critical exponent at 4.95.
Drilling of polymeric materials can be challenging when holes are produced in large scale due to the necessity of controlling the holes quality. This paper presents the effect of machining parameters on the hole quality, in terms of surface roughness and circularity error, in drilling of high density polyethylene, polyamide and polyacetale. The analysis of variance was performed in order to assess the significance of cutting parameter on the hole quality parameters. The experimental results indicate that different cutting conditions are to be employed in order to achieve the optimum surface roughness and circularity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.