A highly ordered hexagonally close-packed nanochannels array was prepared using the self-ordering phenomena during a two-step anodization process of a high purity aluminium foil. The anodized aluminium oxide, with pore diameters of about 280 nm and interpore distances of about 450 nm was prepared as a suspended membrane of about 15 µm thickness on the aluminium frame to which it belongs. The Al 2 O 3 capillaries were bombarded with 3 keV Ne 6+ ions. The first results unambiguously show the existence of ion guiding observed at 5 • and 7.5 • tilt angles of the capillaries compared to the beam direction. To the best of our knowledge, such ion guiding effects of slow ions through hexagonally ordered nanochannels in alumina has not been reported previously.
The development of coating methods that enable us to combine antagonist properties on a single material is a real challenge. This active research topic can impact, for instance, the textile field to engineer fabrics with liquid-repellent properties on one side and superhydrophilic properties on the opposite side. In this context, we have developed an easy surface functionalization process that provides durable Janus wetting properties to fabrics. On the basis of plasma-enhanced chemical vapor deposition (PECVD), we report a simple and reproducible three-step functionalization method that led to a coating with superhydrophobic and superoleophobic properties on one side of the porous substrate and superhydrophilic properties on the opposite side. A thin, fluorinated polymer film was deposited on one side, while the other side was functionalized with a polymer coating made of maleic anhydride, subsequently hydrolyzed to provide carboxylic acid groups to the surface. Static contact angles up to 169° with water and 162° with hexadecane were obtained on the fluorinated side of the fabric thanks to an appropriate combination of surface chemistry with dual-scale surface roughness. In addition, roll-off angles of 6 and 14° with water and hexadecane, respectively, were measured on this side of the sample. As for the opposite side, the hydrolyzed plasma polymer made of maleic anhydride enables us to obtain a surface that fully absorbs water and hexadecane. In addition, these tremendous properties were durable because no significant change was observed after aging and washing cycles. This simple surface functionalization process based on plasma polymerization is an innovative solution for the fabrication of textile with durable waterproof and breathable properties. Besides, the described concept can be adapted to numerous other applications that require Janus properties to porous substrates.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.