The effect of a surface treatment by Nd:YAG laser irradiation on the fatigue behavior of Ti-6Al-4V ELI was studied. Axial fatigue tests were performed to obtain S-N curves in polished and laser treated conditions. Roughness measurements and scanning electron microscopy were used to characterize the features of the modified surface. A reduction in the fatigue strength of around 35% was obtained after the laser treatment of the material surface. Although the surface roughness was in the micrometer scale, a notch effect was suggested to be the reason for the deleterious influence of the laser on the fatigue strength. The reduction in the fatigue strength obligatory demands redesign of implants for laser modified surfaces of Ti-6Al-4V alloy.
Anodizing has proven an effective method for preparing bioactive titanium and has been the subject of many studies regarding the performance and biological characterization of the layers obtained. However, the fatigue behavior of titanium alloys, after undergoing this process is still poorly studied. This study aims to investigate the influence of MAO (Micro-Arc Oxidation) process on the fatigue properties of titanium alloy Ti-6Al-4V. Therefore axial fatigue tests were performed to obtain SxN curves, of specimens in polished and anodized (MAO processed, phosphate salt solution, potential of 290 V) conditions. Roughness measurements, SEM, Raman spectra and X-ray photoelectron spectroscopy (XPS) analyses were used to characterize the features of the modified surface. SEM was also used to analyze the fatigue fractures of the tested specimens. The MAO process, with the parameters used in this investigation, had no influence on the fatigue behavior of the Ti-6Al-4V alloy, when compared to specimens without surface modification.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.