The current work evaluated the microstructures and martensitic transformation temperatures of NiTi shape memory alloy (SMA) deformed by equal channel angular extrusion (ECAE). The Ti-55.27wt.%Ni alloy was processed by 1 ECAE pass at 250 °C using a die with an intersection angle of 120°. After processing, samples were annealed at 300 °C, 400 °C and 500 °C for 1h to evaluate the microstructural changes. Microstructural characterization was performed by scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDS) device, and Vickers hardness measurement. Martensitic transformations temperatures were analyzed by differential scanning calorimetry (DSC). Results show that the annealing treatments presented no significant change in the microstructure of the ECAE processed samples. Meanwhile, the DSC curves corresponding to the annealing treatments performed at 300 °C and 400 °C show two step martensitic transformation related to B2→R→B19'. For the annealing at 500 °C, the martensitic transformation temperatures returned to the ST condition, indicating a reduction of the processing defects.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.