Graphene oxide (GO) has recently become an attractive building block for fabricating graphene-based functional materials. GO films and fibers have been prepared mainly by vacuum filtration and wet spinning. These materials exhibit relatively high Young's moduli but low toughness and a high tendency to tear or break. Here, we report an alternative method, using bar coating and drying of water/GO dispersions, for preparing large-area GO thin films (e.g., 800-1200 cm(2) or larger) with an outstanding mechanical behavior and excellent tear resistance. These dried films were subsequently scrolled to prepare GO fibers with extremely large elongation to fracture (up to 76%), high toughness (up to 17 J/m(3)), and attractive macroscopic properties, such as uniform circular cross section, smooth surface, and great knotability. This method is simple, and after thermal reduction of the GO material, it can render highly electrically conducting graphene-based fibers with values up to 416 S/cm at room temperature. In this context, GO fibers annealed at 2000 °C were also successfully used as electron field emitters operating at low turn on voltages of ca. 0.48 V/μm and high current densities (5.3 A/cm(2)). Robust GO fibers and large-area films with fascinating architectures and outstanding mechanical and electrical properties were prepared with bar coating followed by dry film scrolling.
Activation routes for high surface-area graphene monoliths from graphene oxide colloids, Carbon (2014), doi: http://dx.doi.org/10.1016/j.carbon. 2014.04.071 This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting proof before it is published in its final form. Please note that during the production process errors may be discovered which could affect the content, and all legal disclaimers that apply to the journal pertain. . The mechanism of the porosity development by KOH activation method is proposed.This work provides a promising route for the bottom-up design of pore width-tunable nanoporous carbons.
The prevention of nonspecific protein adsorption is a crucial prerequisite for many biomedical and biotechnological applications. Therefore, the design of robust and versatile methods conferring optimal protein-resistance properties to surfaces has become a challenging issue. Here we report the unexpected case of polycation-ending polyelectrolyte multilayers (PEM) that efficiently prevented the adsorption of a negatively charged model protein, glucose oxidase (GOX). PEM films were based on two typical weak poyelectrolytes: poly(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA). No chemical modification of the polyelectrolytes was required and tunable GOX adsorption was possible by simply changing the buildup pH conditions. Protein-resistance properties are attributed to high film hydration becoming the predominant factor over electrostatic interactions. We explain this effect by oscillations of the internal PAA ionization state throughout the buildup, which results in an excess of carboxylic acid groups within the film. This excess acts as a reservoir of potential carboxylate groups compensating the outer PAH positive charges. Partial results indicated that the system was also resistant to the adsorption of a positively charged protein, lysozyme. Control of the internal ionization of weak polyelectrolyte multilayers might open a route toward simple tuning of protein adsorption. These results should help to rationalize the design of biomaterials, biosensors, or protein separation devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.