Ultra-high molecular weight polyethylene (UHMWPE) and high-density polyethylene (HDPE) blend fibers with the highest tensile strength of 1.13 GPa were prepared by a melt spinning process. The mechanical behavior and crystal structure of the as-spun filaments and fibers were studied by differential scanning calorimetry (DSC), scanning electron microscopy (SEM), X-ray diffraction (XRD), sound velocity orientation testing, and tensile testing. The orientation degree, crystallinity, tensile strength, and initial modulus of the fibers increased with the increasing of the draw ratios. The grain size was shortened in the radial direction and elongated in the axial direction. The results suggested that the improvement of the tensile strength and initial modulus was a result of the compact crystal structure formed by slender grains composed of highly oriented molecular chains. Blending with HDPE could improve the formation of a slender and compact crystal structure, and the tensile strength and initial modulus of the blend fibers were higher.
High-density polyethylene (HDPE) content significantly influences the structure and mechanical properties of ultrahigh molecular weight polyethylene (UHMWPE)/HDPE blend fibers. The molecular chain disentanglement and crystallization characteristics of as-spun filaments and fibers and how the structure affects the final mechanical properties of the fibers were thoroughly studied by adding different contents of HDPE. Dynamic mechanical analysis (DMA) and rheological analysis indicated that the molecular entanglement decreased with increasing HDPE content, improving the UHMWPE melt processability. Sound velocity orientation (SVO) studies indicated that the UHMWPE/HDPE as-spun filaments and fibers with an HDPE content of 40 wt% (U6H4) had a higher molecular chain orientation level. Furthermore, differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) analyses indicated that U6H4 had the highest crystallinity and the thinnest grains in the axial direction, respectively. The compact crystal structure and fully stretched molecular chains of U6H4 yielded the best mechanical properties. The present work disclosed the effect mechanism of HDPE contents on the preparation and properties of UHMWPE/HDPE fibers, which provided an effective and universal strategy for manufacturing high-strength UHMWPE/HDPE fibers with the melt spinning method.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.