The effects of cooling rate and solid mass fraction on the polymorphism, nano and microstructure, thermal and rheological properties of binary mixtures of fully hydrogenated canola oil and canola oil at 208C have been studied. The b-polymorph was observed in fully hydrogenated canola oil (FHCO) when crystallized at slow cooling rates (0.1C8/min), however crystallization at higher cooling rates (0.7 and 108C/min) resulted in the formation of the a form. The b-polymorph was detected in all the binary mixtures of FHCO/canola oil and was not affected by crystallization at different cooling rates. Melting thermograms obtained from 100% FHCO displayed three melting peaks, associated with the development of the b-polymorph via a! b 0 ! b-polymorphic transition in the DSC pan. Some solubilization of solid FHCO into canola oil was observed and the solubility was proportionally higher with increasing liquid oil fraction. The strong influence of the matrix concentration on micro/ nanoscale structure was demonstrated by characterization of crystal size using cryogenic transmission electron (Cryo-TEM) and polarized light microscopy (PLM). Crystallization under higher cooling rates lead to formation of smaller nano and meso-structural elements. Furthermore, oscillatory rheology showed the influence of structural elements' size and polymorphism on material strength. The shear storage modulus (G 0 ) of the mixtures was higher when crystallized at fast cooling rates (108C/min). In contrast, for pure FHCO, G 0 increased by lowering the cooling rate and the highest storage modulus was observed after crystallization at 0.18C/min.

No abstract