The purpose of this dataset is to provide a comparison between synthesized and commercial 4A and 13X type zeolites. Metakaolin produced from the calcination of beneficiated kaolin at 750 °C for 4 h was dealuminated using sulphuric acid to get the required silica to alumina ratio for the zeolite synthesis. Zeolite 4A and 13X samples were characterized along-side with the commercial variants using X-ray fluorescence (XRF), X-ray diffraction (XRD), Brunauer, Emmett and Teller (BET) and scanning electron microscopy (SEM) techniques. These analyses revealed that, the zeolites synthesized are of comparatively acceptable quality. The pore size of 120.859 nm, pore volume of 0.0065 cm3/g and surface area of 22 m2/g were obtained from BET analyses for zeolite 4A synthesized from kaolin, while the commercial zeolite 4A used as control gave pore size of 58.143 nm, pore volume of 0.2462 cm3/g and surface area of 559.13 m2/g. In the same vein, the pore size of 10.5059 nm, pore volume of 0.135847 cm3/g and surface area of 324.584 m2/g were obtained from BET analyses for zeolite 13X synthesized from kaolin, while the commercial zeolite 13X gave pore size of 7.2752 nm, pore volume of 0.135951 cm3/g and surface area of 310.0906 m2/g.
This study is concerned with development and performance evaluation of a mixed-mode solar yam dryer. It was done to address the problems of uneven drying of product on different trays coordinate position in a typical indirect multiple trays dryer. Solar energy drying system was designed using the meteorological conditions of Zaria, Nigeria to dry yam slices in the mixed-mode natural convection. The dryer was designed to dry (7 kg) of yam slices. The dimensions of the dryer were: collector length, collector area, height of the drying chamber, chimney height, length of the drying chamber, and Width of the drying chamber were 0.65 m, 0.27 m2, 0.9 m, 0.7 m, 0.5 m, and 0.43 m, respectively. The solar yam dryer was exposed to solar radiation from 10:00 am to 06:00 pm and tested without load and with yam chips of 5 mm average thickness. Meteorological conditions were monitored during the dehydration process. The average drying rate, collector efficiency and drying efficiency were 2.55 kg/s, 42.20% and 25.35%, respectively. The results of performance evaluation of the solar dryer showed that the drying rate decreases by 3% and 8% in the second and third trays relative to the first tray. This shows that the drying rates did not vary significantly with the coordinate positions of the trays.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.