PURPOSEThe purpose of this study was to compare the coronal bone level and patient satisfaction in 1-implant and 2-implant assisted mandibular overdentures.MATERIALS AND METHODSTwenty patients who had maladaptive mandibular dentures were treated in this study. Patients were randomly divided into two groups. The first group received 1 implant (Simple line II, Implantium, South Korea) in their mandibular midline and the second group received 2 implants in their B and D regions (according to Misch's category). If the primary stability of each implant was at least 60 ISQ, ball attachment was placed and denture relined with soft liner. After 6 weeks, retentive cap incorporated with hard acrylic resin. In the 6 and 12 months recalls, periapical digital radiograph were made and visual analogue scale questionnaires were used to record patient satisfaction. The Friedman test was done for comparing the presurgical and postsurgical parameters in each group and the U-Mann Whitney test (P<.05) was done for comparison of post-treatment results between the two groups.RESULTSAll implants achieved sufficient primary stability to be immediately loaded. Patient satisfaction was high, and there were no significant differences between two groups (P>.05). In addition, mean marginal bone loss was 0.6 ± 0.67 mm in the first group and 0.6 ± 0.51 mm in the second group, after 12 month. Mean marginal bone loss showed no significant differences between two groups.CONCLUSIONThis preliminary one-year result indicated that mandibular overdentures anchored to a single implant can be a safe and cost-effective method as a starting step for implant-overdenture treatment.
ObjectivesIt is difficult to achieve adhesion between resin cement and zirconia ceramics using routine surface preparation methods. The aim of this study was to evaluate the effects of CO2 and Er:YAG laser treatment on the bond strength of resin cement to zirconia ceramics.Materials and MethodsIn this in-vitro study 45 zirconia disks (6 mm in diameter and 2 mm in thickness) were assigned to 3 groups (n = 15). In control group (CNT) no laser treatment was used. In groups COL and EYL, CO2 and Er:YAG lasers were used for pretreatment of zirconia surface, respectively. Composite resin disks were cemented on zirconia disk using dual-curing resin cement. Shear bond strength tests were performed at a crosshead speed of 0.5 mm/min after 24 hr distilled water storage. Data were analyzed by one-way ANOVA and post hoc Tukey's HSD tests.ResultsThe means and standard deviations of shear bond strength values in the EYL, COL and CNT groups were 8.65 ± 1.75, 12.12 ± 3.02, and 5.97 ± 1.14 MPa, respectively. Data showed that application of CO2 and Er:YAG lasers resulted in a significant higher shear bond strength of resin cement to zirconia ceramics (p < 0.0001). The highest bond strength was recorded in the COL group (p < 0.0001). In the CNT group all the failures were adhesive. However, in the laser groups, 80% of the failures were of the adhesive type.ConclusionsPretreatment of zirconia ceramic via CO2 and Er:YAG laser improves the bond strength of resin cement to zirconia ceramic, with higher bond strength values in the CO2 laser treated samples.
Objectives: This study aimed to assess the effect of three commonly consumed beverages on surface roughness of polished and glazed zirconia-reinforced lithium silicate (ZLS) glass ceramics.
Materials and Methods: In this experimental study, 104 rectangular specimens were cut from Vita Suprinity blocks with 2 mm thickness. After ultrasonic cleaning and firing of the specimens, they were finished and polished in two groups. Specimens in the first group were polished using a 2-step polishing kit while the second group specimens were glazed and heated in a porcelain firing oven according to the manufacturer’s instructions. Baseline surface roughness was measured using a profilometer. Specimens in each group were then randomly divided into 4 subgroups (n=13) for immersion in artificial saliva (control group), cola, orange juice and black tea. Surface roughness was measured again and data were analyzed using two-way ANOVA.
Results: The highest and the lowest mean Ra were found in orange juice and saliva subgroups, respectively in both glazed and polished groups. The Ra values of both polished and glazed groups significantly increased after immersion in orange juice and cola (P<0.05). The polished surfaces showed insignificantly higher surface roughness compared with glazed surfaces (P>0.05).
Conclusion: Orange juice and cola significantly increased the surface roughness of both polished and glazed ZLS ceramics. Type of surface finishing (polishing versus glazing) had no significant effect on the surface roughness of specimens following immersion in different beverages.
Background. Recently, non-presintered chromium-cobalt (Cr-Co) blocks with the commercial name of Ceramill Sintron were introduced to the market. However, comprehensive studies on the dimensional accuracy and fit of multi-unit frameworks made of these blocks using the coordinate measuring machine (CMM) are lacking. This study aimed to assess and compare the dimensional changes and fit of conventional casting and milled frameworks using Ceramill Sintron.
Methods. A metal model was designed and scanned and 5-unit frameworks were fabricated using two techniques: (I) the conventional casting method (n=20): the wax model was designed, milled in the CAD/CAM machine, flasked and invested; (II) the milling method using Ceramill Sintron blocks (n=20): the wax patterns of group 1 were used; Ceramill Sintron blocks were milled and sintered. Measurements were made on the original reference model and the fabricated frameworks using the CMM in all the three spatial dimensions, and dimensional changes were recorded in a checklist. Data were analyzed with descriptive statistics, and the two groups were compared using one-way ANOVA and Tukey test (α=0.05).
Results. The fabricated frameworks in both groups showed significant dimensional changes in all the three dimensions. Comparison of dimensional changes between the two groups revealed no significant differences (P>0.05) except for transverse changes (arch) that were significantly greater in Ceramill Sintron frameworks (P<0.05).
Conclusion. The two manufacturing processes were the same regarding dimensional changes and the magnitude of marginal gaps and both processes resulted in significant dimensional changes in frameworks. Ceramill Sintron frameworks showed significantly greater transverse changes than the conventional frameworks.
Background
This study aimed to compare the amount of artifacts induced by the titanium and zirconium implants on cone-beam computed tomography (CBCT) and assess the effect of different exposure settings on the image quality for both materials.
Methods
In this experimental study, 30 zirconium and 30 titanium implants were placed in bovine rib bone blocks. CBCT images were taken in two different fields of view (FOV: 4 × 6 cm2 and 6 × 8 cm2) and at two resolutions (133 µ and 200 µ voxel size). Subsequently, two observers assessed the images and detected the amount of artifacts around the implants through gray values. Data were analyzed by paired t test and independent t test using SPSS 21 and the 0.05 significance level.
Results
The results showed that titanium implants caused lower amounts of artifacts than zirconium implants, which was statistically significant (P < 0.001). The larger FOV (6 × 8 cm2) resulted in a lower amount of artifacts in both groups, although the results were only statistically significant in the zirconium group (P < 0.001). The amount of artifacts was increased when using the 133 µ voxel size in both groups, which was only significant in the zirconium group (P < 0.001).
Conclusion
Our results suggest that zirconium implants induce higher amounts of artifacts than titanium ones. We also concluded that the artifacts could be minimized using the larger FOV and voxel size.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.