This study investigates the comparison of the microstructural and mechanical properties of a novel ternary reinforced AA7075 hybrid metal matrix composite. Four samples, including AA7075 (base alloy), AA7075-5wt %SiC (MMC), AA7075-5wt %SiC-3wt %RHA (s-HMMC), and AA7075-5wt %SiC-3wt %RHA-1wt %CES (n-HMMC) were developed using the stir casting liquid metallurgy route, followed by the heat treatment. The experimental densities corresponded with the theoretical values, confirming the successful fabrication of the samples. A minimum density of 2714 kg/m3 was recorded for the n-HMMC. In addition, the highest porosity of 3.11% was found for n-HMMC. Furthermore, an increase of 24.4% in ultimate tensile strength and 32.8% in hardness of the n-HMMC was recorded compared to the base alloy. However, its ductility and impact strength was compromised with the lower values of 5.98% and 1.5 J, respectively. This was confirmed by microstructural analysis, which reveals that n-HMMC has mixing issues and forms agglomerates in the matrix, which served as the potential sites of stress concentration leading to low impact strength and ductility. Nevertheless, the hybrid composites showed superior mechanical properties over the MMC and its base alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.