Purpose
The aim of this study is to determine the optimal parameters for friction coefficient of kenaf/epoxy (KE) composite as an alternative friction material.
Design/methodology/approach
The design of experiment was constructed using the Taguchi method. KE specimens were formed into 10 mm diameter pins using hot compression technique with different types, weight concentrations and treatments of kenaf. The samples were tested using a pin-on-disc tribometer at different applied loads, speeds and operating temperatures with a constant sliding distance of 3 km under dry sliding conditions.
Findings
The sample with 45 wt.% of non-treated kenaf fibre, tested at 19.62 N, 500 rpm and 100°C was found to be the optimized combination to obtain higher friction. From the confirmation test, the experimental friction coefficient is acceptable because of fall within 95 per cent confidence interval. Predominant wear mechanisms are identified as micro-crack and debonding of fibre.
Originality/value
KE composite can be considered as an alternative friction material, as the tested friction coefficient is within the suggested range for the friction material applications.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.