Objective: The purpose of this study was to demonstrate the effect of low-level laser therapy (LLLT) on the peri-implant bone healing process in the rabbit mandible. Background data: LLLT has been shown to accelerate tissue repair and osseointegration of implants placed into the rabbit tibia. However, the beneficial effects of LLLT have never been tested in the rabbit mandible, which would more closely mimic the human situation. Materials and methods: Twenty-four male New Zealand rabbits were randomly divided into four groups of six animals each. All animals had their left mandibular incisors extracted, followed by immediate insertion of a titanium dental implant in the fresh socket. Three groups received LLLT [aluminum-galliumarsenide (AlGaAs), k = 830nm, 50 mW, continuous wave (CW)] at three different energy densities per treatment session (E-5, 5 J/cm 2 ; E-10, 10 J/cm 2 ; and E-20, 20 J/cm 2 ). Irradiation was performed every 48 h for 13 days, totaling seven sessions. One group received sham treatment (controls). Histological sections were obtained from each of the 24 mandibles dissected, without first decalcifying the specimens, and were stained with hematoxylin and eosin and Picrosirius red for histomorphometric evaluation. Bone-to-implant contact (BIC), bone formation area, and collagen fiber area were assessed by light microscopy. Results: Significant differences were found between group E-20 and all other groups ( p < 0.05). Histomorphometric evaluation showed significantly higher BIC and significantly more collagen fibers in group E-20. Conclusions: Photobiostimulation with LLLT at an energy density of 20 J/cm 2 per session had a significant positive effect on new bone formation around dental implants inserted in the rabbit mandible.
This study evaluated the use of red and infrared lasers on tissue surrounding the femurs of 60 rats randomly divided into three groups after implantation of bioabsorbable plates. The control group were not subjected to laser irradiation; group A was treated with red laser [indium-gallium-aluminum-phosphide (InGaAlP) laser, wavelength 685 nm, 35 mW, continuous wave (CW), Ø = 0.06 cm, 2.23 min], and group B was subjected to infrared laser [gallium-aluminum-arsenium (GaAlAs) laser, wavelength 830 nm, 50 mw, CW, Ø = 0.06 cm, 1.41 min], both at 10 J/cm(2). Samples were stained with hematoxylin and eosin (H&E) and examined microscopically. Results showed that the laser irradiation had had a positive photobiomodulation effect on inflammation, confirmed by a better histologic pattern than that of the control group at 3 days and 7 days. Semiquantitative analysis revealed that groups A and B had a histologic score significantly greater than that of the control group at 3 days. At 21 days, histomorphometric analysis revealed a more intense inflammation in the red laser group than in the other groups. We concluded that low-level laser therapy (LLLT) has positive effects on the photobiomodulation of inflammation in the tissues surrounding the poly-L-lactic/polyglycolic acid (PLLA/PGA) bioabsorbable plate. It stimulated vascularization, fibroblast proliferation, and collagen deposition.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.