The lignin component found in both water insoluble (WI) and water and alkali insoluble (WIA) fractions derived from SO(2)-impregnated steam-exploded eucalyptus chips (SEE) was isolated and characterized. Dioxane lignins with a sugar content lower than 2% (w/w) were obtained after each material was treated with commercial cellulases. The C9 formulas of both SEE-WI and SEE-WIA dioxane lignins were C(9)H(6.83)N(0.04)O(2.24)(OCH(3))(1.21)(OH(aro))(0.56)(OH(ali))(0. 77) and C(9)H(8.65)N(0.29)O(1.97)(OCH(3))(0.90)(OH(aro))(0. 46)(OH(ali))(1.02), respectively. The weight-average molecular weight (M(w)) of the SEE-WI lignin corresponded to 3.85 kDa, whereas the SEE-WIA lignin had an M(w) of 3.66 kDa for the same polydispersity of 2.4. The SEE-WIA lignin was shown to be more thermally stable than the SEE-WI lignin, requiring temperatures in the range of 520 degrees C for complete degradation. FTIR and (1)H NMR analyses of both untreated and peracetylated lignin fractions showed that (a) the alkali insoluble lignin contained a relatively higher degree of substitution in aromatic rings per C9 unit and that (b) alkaline extraction removed lignin fragments containing appreciable amounts of phenolic hydroxyl groups.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.