The kinetic arrest of martensitic transformation (MT) has been observed in as-solidified Ni52.2Mn34.3In13.5 melt spun ribbons. The main characteristics of this unusual field-induced magneto-structural phenomenon have been determined through a dc magnetization study. The sample studied was fabricated by rapid solidification using the melt spinning technique at a high quenching rate of 48 ms-1. At room temperature, it is a single phase austenite (AST) with the bcc B2-type crystal structure and Curie temperature of TCA=285 K. With decreasing temperature, the austenite phase transforms into the martensite phase (MST) with TCM≈185 K at a starting martensitic transition temperature of MS=275 K. A moderate but progressive kinetic arrest of the AST to MST transformation has been observed for magnetic field values above H=10 kOe and was studied up to Hmax= 90 kOe. The metastable character of the non-equilibrium field-cooled state is revealed by the decreasing behavior of the saturation magnetization under a large magnetic field of 50 kOe after temperature cycling from 10 K to 150 K. The total magnetization difference Δσ between the zero field-cooling and field-cooling pathways of the temperature dependence of magnetization shows irreversible and reversible components and the former decreases with decreasing temperature.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.