In addition to locally stressed rhombohedral phase, evidence for trapped metastable phases in (001)-cut single-crystal wafers of Pb(Zn1/3Nb2/3)O3–(8–9)%PbTiO3 has been obtained by means of the x-ray diffraction technique. The rhombohedral phase is stressed predominantly in compression in the plane of the wafer, both in unpoled and poled conditions, giving rise to the broad shoulder at the lower 2θ end of the rhombohedral peak. Trapped tetragonal phase, with its c axis lying both in the plane and perpendicular to the plane of the wafer, can also be detected in as-sliced, unpoled wafers. Upon poling along the [001] thickness direction, the tetragonal phase with its c axis lying in the plane of the wafer is transformed readily to the rhombohedral phase. In contrast, a minute amount of tetragonal phase with its c axis perpendicular to the plane of the wafer can be stabilized by the stressed rhombohedral matrix in poled state. At sufficiently high poling fields (i.e., ⩾1.2 kV/mm), a trapped pseudomonoclinic phase may be formed among the locally stressed rhombohedral lattice.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.