Smart materials like piezoelectric polymers represent a new class of promising scaffold in neural tissue engineering. In the current study, the fabrication processing parameters of polyvinylidine fluoride (PVDF) nanofibrous scaffold are found as a potential scaffold with nanoscale morphology and microscale alignment. Electrospinning technique with the ability to mimic the structure and function of an extracellular matrix is a preferable method to customize the scaffold features. PVDF nanofibrous scaffolds were successfully fabricated by the electrospinning technique. The influence of PVDF solution concentration and other processing parameters like applied voltage, tip-to-collector distance, feeding rate, collector speed and the solvent were studied. The optimal parameters were 30 w/v% PVDF concentration, 15 kV applied voltage, 18 cm tip-to-collector distance, 0.5 ml/h feeding rate, 2500 rpm collector speed and N,N′-dimethylacetamide/acetone as a solvent. The mean fiber diameter of the obtained scaffold was 352.9 ± 24 nm with uniform and aligned morphology. Finally, the cell viability and morphology of PC-12 cells on the optimum scaffold indicated the potential of PVDF nanofibrous scaffold for neural tissue engineering.

Silver nanoparticles were produced by irradiating a silver plate with 1064 nm laser beam in pure water. The effect of the laser fluence and ablation time on the ablation efficiency was studied. Fragmentation of the ablated colloid solution by subsequent treatment with 1064 and 532 nm laser pulses yield redistribution of nanoparticles to a smaller mean size.

In this study, gold nanoparticles/Polyvinylidenefluoride (PVDF) composite electrospun mat with enhanced piezoelectricity were fabricated and characterized. Gold colloidal nanoparticles (Au NPs) were prepared via laser ablation of metallic targets in liquid media. The active Q-switched Nd:YAG laser was used as an irradiation source. Then, PVDF was dissolved in Au NPs colloidal solution at 30% wt for the synthesis of Au NPs/PVDF composite nanofibers by electrospinning. The optical absorbance spectra of Au NPS and the polymeric solutions were obtained by the UV-Visible spectroscopy. Moreover, the morphology of Au NPS, nanostructures of fibers and diameter size distribution of nanofibers were analyzed by Scanning Electron Microscopy, Field Emission Scanning Electron Microscopy, and Transmitted Electron Microscopy methods. The crystallinity and piezoelectricity of PVDF and Au NPs/PVDF composite nanofibers mats were measured by X-Ray Diffraction and Fourier Transform Infrared methods. Subsequently, in vitro cytocompatibility was evaluated by MTT assay and the attachment and morphology of PC-12 cells cultured on scaffolds were studied. It was found that laser ablated Au NPs can be used in electrospun nanofibers of PVDF with adequate structural properties and increase piezoelectricity of nanofibers which might be suitable for applying as nerve tissue engineering scaffolds. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1984-1993, 2017.

No abstract

The dynamics of Au/Ag alloy formation under Nd:YAG laser irradiation of a mixture of the monometallic colloidal solutions have been experimentally investigated. The change in absorption spectrum of the colloidal particles has been studied as a function of laser irradiation time, fluence, and concentration of nanoparticles in individual colloids. The characteristic time of the alloy formation is about 10 minutes, without any surfactant.

No abstract

No abstract

No abstract