Recent observation of high density polarization-induced two-dimensional electron gases in ultra-thin N-polar GaN layers grown on single-crystal AlN has enabled the development of N-polar high electron mobility transistors (HEMTs) on AlN. Such devices will take advantage of thermal and power handling capabilities of AlN, while simultaneously benefitting from the merits of N-polar structures, such as a strong back barrier. We report the experimental demonstration of N-polar GaN/AlGaN/AlN HEMTs on single-crystal AlN substrates, showing an on-current of 2.6 A/mm with a peak transconductance of 0.31 S/mm. Small-signal RF measurements revealed speeds exceeding ft/ fmax = 68/100 GHz. These results pave the way for developing RF electronics with excellent thermal management based on N-polar single-crystal AlN.
We present a compositional dependence study of electrical characteristics of AlxGa1−xN quantum well channel-based AlN/AlGaN/AlN high electron mobility transistors (HEMTs) with x=0.25,0.44, and 0.58. This ultra-wide bandgap heterostructure is a candidate for next-generation radio frequency and power electronics. The use of selectively regrown n-type GaN Ohmic contacts results in contact resistance that increases as the Al content of the channel increases. The DC HEMT device characteristics reveal that the maximum drain current densities progressively reduce from 280 to 30 to 1.7 mA/mm for x=0.25,0.44, and 0.58, respectively. This is accompanied by a simultaneous decrease (in magnitude) in threshold voltage from −5.2 to −4.9 to −2.4 V for the three HEMTs. This systematic experimental study of the effects of Al composition x on the transistor characteristics provides valuable insights for engineering AlGaN channel HEMTs on AlN for extreme electronics at high voltages and high temperatures.
Polarization-induced carriers play an important role in achieving high electrical conductivity in ultrawide bandgap semiconductor AlGaN, which is essential for various applications ranging from radio frequency and power electronics to deep UV photonics. Despite significant scientific and technological interest, studies on polarization-induced carriers in N-polar AlGaN are rare. We report the observation and properties of polarization-induced two-dimensional electron gases (2DEGs) in N-polar AlGaN/AlN heterostructures on single-crystal AlN substrates by systematically varying the Al content in the 8 nm top layers from x = 0 to x = 0.6, spanning energy bandgaps from 3.56 to 4.77 eV. The 2DEG density drops monotonically with increasing Al content, from 3.8 × 1013/cm2 in the GaN channel, down to no measurable conductivity for x = 0.6. Alloy scattering limits the 2DEG mobility to below 50 cm2/V s for x = 0.49. These results provide valuable insights for designing N-polar AlGaN channel high electron mobility transistors on AlN for extreme electronics at high voltages and high temperatures, and for UV photonic devices.
The polarization difference and band offset between Al(Ga)N and GaN induce two-dimensional (2D) free carriers in Al(Ga)N/GaN heterojunctions without any chemical doping. A high-density 2D electron gas (2DEG), analogous to the recently discovered 2D hole gas in a metal-polar structure, is predicted in a N-polar pseudomorphic GaN/Al(Ga)N heterostructure on unstrained AlN. We report the observation of such 2DEGs in N-polar undoped pseudomorphic GaN/AlGaN heterostructures on single-crystal AlN substrates by molecular beam epitaxy. With a high electron density of ∼4.3 [Formula: see text]/cm2 that maintains down to cryogenic temperatures and a room temperature electron mobility of ∼450 cm2/V s, a sheet resistance as low as ∼320 [Formula: see text] is achieved in a structure with an 8 nm GaN layer. These results indicate significant potential of AlN platform for future high-power RF electronics based on N-polar III-nitride high electron mobility transistors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.