The potential for decellularized aortic heart valves (AVs) as heart valve replacements is based on the assumption that the major cellular immunogenic components have been removed, and that the remaining extracellular matrix (ECM) should retain the necessary mechanical properties and functional design. However, decellularization processes likely alter the ECM mechanical and structural properties, potentially affecting long term durability. In the present study we explored the effects of an anionic detergent (SDS), enzymatic agent (Trypsin), and a non-ionic detergent (Triton X-100) on the mechanical and structural properties of AV leaflets (AVLs) to provide greater insight into the initial functional state of the decellularized AVL. The overall extensibility represented by the areal strain under 60 N/m increased from 68.85% for the native AV to 139.95%, 137.51%, and 177.69% for SDS, Trypsin, and Triton X-100, respectively, after decellularization. In flexure, decellularized AVLs demonstrated a profound loss of stiffness overall, and also produced a nonlinear moment-curvature relation compared to the linear response of the native AVL. Effective flexural moduli decreased from 156.0±24.6 kPa for the native AV to 23.5±5.8 kPa, 15.6±4.8 kPa, and 19.4 ±8.9 kPa for SDS, Trypsin, and Triton X-100 treated leaflets, respectively. While the overall leaflet fiber architecture remained relatively unchanged, decellularization resulted in substantial microscopic disruption. In conclusion, changes in mechanical and structural properties of decellularized leaflets were likely associated with disruption of the ECM, which may impact the durability of the leaflets.

The collagen fiber alignment and biomechanical behavior of naturally occurring extracellular matrix (ECM) scaffolds are important considerations for the design of medical devices from these materials. Both should be considered in order to produce a device to meet tissue specific mechanical requirements (e.g., tendon vs. urinary bladder), and could ultimately affect the remodeling response in vivo. The present study evaluated the collagen fiber alignment and biaxial mechanical behavior of ECM scaffold material harvested from porcine urinary bladder tunica mucosa and basement membrane (together referred to as urinary bladder matrix (UBM)) and ECM harvested from urinary bladder submucosa (UBS). Since the preparation of UBM allows for control of the direction of delamination, the effect of the delamination method on the mechanical behavior of UBM was determined by delaminating the submucosa and other abluminal layers by scraping along the longitudinal axis of the bladder (apex to neck) (UBML) or along the circumferential direction (UBMC). The processing of UBS does not allow for similar directional control. UBML and UBS had similar collagen fiber distributions, with a preferred collagen fiber alignment along the longitudinal direction. UBMC showed a more homogenous collagen fiber orientation. All samples showed a stiffer mechanical behavior in the longitudinal direction. Despite similar collagen fiber distributions, UBML and UBS showed quite different mechanical behavior for the applied loading patterns with UBS showing a much more pronounced toe region. The mechanical behavior for UBMC in both directions was similar to the mechanical behavior of UBML. There are distinct differences in the mechanical behavior of different layers of ECM from the porcine urinary bladder, and the processing methods can substantially alter the mechanical behavior observed.

Recently, major achievements in creating decellularized whole tissue scaffolds have drawn considerable attention to decellularization as a promising approach for tissue engineering. Decellularized tissues are expected to have mechanical strength and structure similar to the native tissues from which they are derived. However, numerous studies have shown that mechanical properties change after decellularization. Often, tissue structure is observed by histology and electron microscopy, but the structural alterations that may have occurred are not always evident. Here, a variety of techniques were used to investigate changes in tissue structure and relate them to altered mechanical behavior in decellularized rabbit carotid arteries. Histology and scanning electrom microscopy revealed that major extracellular matrix components were preserved and fibers appeared intact, although collagen appeared looser and less crimped after decellularization. Transmission electrom microscopy confirmed the presence of proteoglycans (PG), but there was decreased PG density and increased spacing between collagen fibrils. Mechanical testing and opening angle measurements showed that decellularized arteries had significantly increased stiffness, decreased extensibility and decreased residual stress compared with native arteries. Small-angle light scattering revealed that fibers had increased mobility and that structural integrity was compromised in decellularized arteries. Taken together, these studies revealed structural alterations that could be related to changes in mechanical properties. Further studies are warranted to determine the specific effects of different decellularization methods on the structure and performance of decellularized arteries used as vascular grafts.

Background-Defects in the pulmonary valve (PV) occur in a variety of forms of congenital heart diseases. Quantitative information on PV collagen fiber architecture, and particularly its response to diastolic forces, is necessary for the design and functional assessment of approaches for PV repair and replacement. This is especially the case for novel tissue engineered PV, which rely on extensive in-vivo remodeling for long-term function.