Nata de coco (NDC), a bacterial cellulose formed by Acetobacter xylinum, was utilized to fabricate a membrane via acetylation and phase inversion methods. The NDC was activated and dissolved in N,N-Dimethylacetamide (DMAc) with lithium chloride (LiCl) at varying amounts of NDC, LiCl/DMAc ratio, activation temperature, and dissolution temperature. Acetylation was done by adding acetic anhydride (in a mass ratio of 1:12 NDC-anhydride) to NDC-DMAc/LiCl solution at a dissolution temperature of 110 °C for 3 hours. The modified-NDC was recovered via precipitation in methanol. The modified-NDC was washed with deionized water then freeze-dried. Modification was verified by determining the degree of substitution (DS) using titration and FTIR analysis. It was observed that the modification could be carried out at an NDC/DMAc (w/v) ratio of 1:75 at 120 °C for 1 hour, and addition of 8% (w/v) LiCl catalyst at 110 °C for 20 minutes. The DS of the modified-NDC was observed in the range of 2.84 – 3.69, which indicates a successful modification. This was further verified by the FTIR results. Membrane fabrication was carried out using the modified-NDC via immersion-precipitation and solvent evaporation methods. A successful membrane formation was observed using solvent evaporation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.