Here, we show that the aerosol assisted chemical vapor deposition process is suitable for growing single crystalline tungsten oxide nanowires loaded with nickel oxide nanoparticles.

The properties of multi-wall carbon nanotubes decorated with iridium oxide nanoparticles (IrOx-MWCNTs) are studied to detect harmful gases such as nitrogen dioxide and ammonia. IrOx nanoparticles were synthetized using a two-step method, based on a hydrolysis and acid condensation growth mechanism. The metal oxide nanoparticles obtained were employed for decorating the sidewalls of carbon nanotubes. Iridium-oxide nanoparticle decorated carbon nanotube material showed higher and more stable responses towards NH3 and NO2 than bare carbon nanotubes under different experimental conditions, establishing the optimal operating temperatures and estimating the limits of detection and quantification. Furthermore, the nanomaterials employed were studied using different morphological and compositional characterization techniques and a gas sensing mechanism is proposed.

An organic–inorganic heterojunction with an n-type behavior to detect ammonia in a humid atmosphere.

Indium oxide octahedral nanopowders were obtained from an ionic precursor compound after an oxidation process conducted under a low-oxygen atmosphere. This method was found to produce contamination-free indium oxide nanomaterial with very similar morphological and crystalline properties to the one produced by vapor-phase transport, but at significantly lower temperatures and higher yield. The as-synthesized indium oxide was mixed to an organic vehicle and microdrop deposited to form a film bridging the interdigitated silver electrodes patterned on top of a flexible, polyimide (Kapton®), substrate. The gas sensing properties of the flexible chemoresistors towards ammonia vapors, hydrogen, and nitrogen dioxide were investigated. It was found that these sensors were remarkably sensitive to nitrogen dioxide at a low operating temperature of 150 °C. These results are consistent with the performance of vapor-phase transport synthesized indium oxide octahedra sensors on rigid, ceramic substrates. Therefore, the results presented here pave the way for the mass production of inexpensive gas sensors onto flexible substrates via additive manufacturing.

No abstract

No abstract

No abstract

No abstract