In this study cutinases from Thermobifida cellulosilytica DSM44535 (Thc_Cut1 and Thc_Cut2) and Thermobifida fusca DSM44342 (Thf42_Cut1) hydrolyzing poly(ethylene terephthalate) (PET) were successfully cloned and expressed in E.coli BL21-Gold(DE3). Their ability to hydrolyze PET was compared with other enzymes hydrolyzing natural polyesters, including the PHA depolymerase (ePhaZmcl) from Pseudomonas fluorescens and two cutinases from T. fusca KW3. The three isolated Thermobifida cutinases are very similar (only a maximum of 18 amino acid differences) but yet had different kinetic parameters on soluble substrates. Their k cat and K m values on pNP–acetate were in the ranges 2.4–211.9 s–1 and 127–200 μM while on pNP–butyrate they showed k cat and K m values between 5.3 and 195.1 s–1 and between 1483 and 2133 μM. Thc_Cut1 released highest amounts of MHET and terephthalic acid from PET and bis(benzoyloxyethyl) terephthalate (3PET) with the highest concomitant increase in PET hydrophilicity as indicated by water contact angle (WCA) decreases. FTIR-ATR analysis revealed an increase in the crystallinity index A 1340/A 1410 upon enzyme treatment and an increase of the amount of carboxylic and hydroxylic was measured using derivatization with 2-(bromomethyl)naphthalene. Modeling the covalently bound tetrahedral intermediate consisting of cutinase and 3PET indicated that the active site His-209 is in the proximity of the O of the substrate thus allowing hydrolysis. On the other hand, the models indicated that regions of Thc_Cut1 and Thc_Cut2 which differed in electrostatic and in hydrophobic surface properties were able to reach/interact with PET which may explain their different hydrolysis efficiencies.

A cutinase from Thermomyces cellullosylitica (Thc_Cut1), hydrolyzing the synthetic polymer polyethylene terephthalate (PET), was fused with two different binding modules to improve sorption and thereby hydrolysis. The binding modules were from cellobiohydrolase I from Hypocrea jecorina (CBM) and from a polyhydroxyalkanoate depolymerase from Alcaligenes faecalis (PBM). Although both binding modules have a hydrophobic nature, it was possible to express the proteins in E. coli . Both fusion enzymes and the native one had comparable kcat values in the range of 311 to 342 s(-1) on pNP-butyrate, while the catalytic efficiencies kcat/Km decreased from 0.41 s(-1)/ μM (native enzyme) to 0.21 and 0.33 s(-1)/μM for Thc_Cut1+PBM and Thc_Cut1+CBM, respectively. The fusion enzymes were active both on the insoluble PET model substrate bis(benzoyloxyethyl) terephthalate (3PET) and on PET although the hydrolysis pattern was differed when compared to Thc_Cut1. Enhanced adsorption of the fusion enzymes was visible by chemiluminescence after incubation with a 6xHisTag specific horseradish peroxidase (HRP) labeled probe. Increased adsorption to PET by the fusion enzymes was confirmed with Quarz Crystal Microbalance (QCM-D) analysis and indeed resulted in enhanced hydrolysis activity (3.8× for Thc_Cut1+CBM) on PET, as quantified, based on released mono/oligomers.

From a screening on agar plates with bis(benzoyloxyethyl) terephthalate (3PET), a Bacillus subtilis p-nitrobenzylesterase (BsEstB) was isolated and demonstrated to hydrolyze polyethyleneterephthalate (PET). PET-hydrolase active strains produced clearing zones and led to the release of the 3PET hydrolysis products terephthalic acid (TA), benzoic acid (BA), 2-hydroxyethyl benzoate (HEB), and mono-(2-hydroxyethyl) terephthalate (MHET) in 3PET supplemented liquid cultures. The 3PET-hydrolase was isolated from non-denaturating polyacrylamide gels using fluorescein diacetate (FDA) and identified as BsEstB by LC-MS/MS analysis. BsEstB was expressed in Escherichia coli with C-terminally fused StrepTag II for purification. The tagged enzyme had a molecular mass of 55.2 kDa and a specific activity of 77 U/mg on p-nitrophenyl acetate and 108 U/mg on p-nitrophenyl butyrate. BsEstB was most active at 40°C and pH 7.0 and stable for several days at pH 7.0 and 37°C while the half-life times decreased to 3 days at 40°C and only 6 h at 45°C. From 3PET, BsEstB released TA, MHET, and BA, but neither bis(2-hydroxyethyl) terephthalate (BHET) nor hydroxyethylbenzoate (HEB). The kcat values decreased with increasing complexity of the substrate from 6 and 8 (s-1) for p-nitrophenyl-acetate (4NPA) and p-nitrophenyl-butyrate (4NPB), respectively, to 0.14 (s-1) for bis(2-hydroxyethyl) terephthalate (BHET). The enzyme hydrolyzed PET films releasing TA and MHET with a concomitant decrease of the water-contact angle (WCA) from 68.2°±1.7° to 62.6°±1.1° due to formation of novel hydroxyl and carboxyl groups. These data correlated with a fluorescence emission intensity increase seen for the enzyme treated sample after derivatization with 2-(bromomethyl)naphthalene.

Abstract:A new esterase from Thermobifida halotolerans (Thh_Est) was cloned and expressed in E. coli and investigated for surface hydrolysis of polylactic acid (PLA) and polyethylene terephthalate (PET). Thh_Est is a member of the serine hydrolases superfamily containing the -GxSxG-motif with 85-87% homology to an esterase from T. alba, to an acetylxylan esterase from T. fusca and to various Thermobifida cutinases. Thh_Est hydrolyzed the PET model substrate bis(benzoyloxyethyl)terephthalate and PET releasing terephthalic acid and mono-(2-hydroxyethyl) terephthalate in comparable amounts (19.8 and 21.5 mmol/mol of enzyme) while no higher oligomers like bis-(2-hydroxyethyl) terephthalate were detected. Similarly, PLA was hydrolyzed as indicated by the release of lactic acid. Enzymatic surface hydrolysis of PET and PLA led to a strong hydrophilicity increase, as quantified with a WCA decrease from 90.8° and 75.5° to 50.4° and to a complete spread of the water drop on the surface, respectively. OPEN ACCESSPolymers 2012, 4 618

g Cutinases have shown potential for hydrolysis of the recalcitrant synthetic polymer polyethylene terephthalate (PET). We have shown previously that the rate of this hydrolysis can be enhanced by the addition of hydrophobins, small fungal proteins that can alter the physicochemical properties of surfaces. Here we have investigated whether the PET-hydrolyzing activity of a bacterial cutinase from Thermobifida cellulosilytica (Thc_Cut1) would be further enhanced by fusion to one of three Trichoderma hydrophobins, i.e., the class II hydrophobins HFB4 and HFB7 and the pseudo-class I hydrophobin HFB9b. The fusion enzymes exhibited decreased k cat values on soluble substrates (p-nitrophenyl acetate and p-nitrophenyl butyrate) and strongly decreased the hydrophilicity of glass but caused only small changes in the hydrophobicity of PET. When the enzyme was fused to HFB4 or HFB7, the hydrolysis of PET was enhanced >16-fold over the level with the free enzyme, while a mixture of the enzyme and the hydrophobins led only to a 4-fold increase at most. Fusion with the non-class II hydrophobin HFB9b did not increase the rate of hydrolysis over that of the enzyme-hydrophobin mixture, but HFB9b performed best when PET was preincubated with the hydrophobins before enzyme treatment. The pattern of hydrolysis by the fusion enzymes differed from that of Thc_Cut1 as the concentration of the product mono(2-hydroxyethyl) terephthalate relative to that of the main product, terephthalic acid, increased. Small-angle X-ray scattering (SAXS) analysis revealed an increased scattering contrast of the fusion proteins over that of the free proteins, suggesting a change in conformation or enhanced protein aggregation. Our data show that the level of hydrolysis of PET by cutinase can be significantly increased by fusion to hydrophobins. The data further suggest that this likely involves binding of the hydrophobins to the cutinase and changes in the conformation of its active center. P olyethylene terephthalate (PET) is the best-known and most widespread synthetic polyester in the world. It is used for foils and bottles as well as for fibers for the textile industry (1). Recycling of PET and modification of its properties for different applications by traditional procedures involve harsh chemical and physicochemical treatments (2, 3). Enzymatic modification, particularly by cutinases, has been recognized as a powerful alternative in the past decade (4, 5) and, besides offering new avenues for PET recycling, has the additional advantage of creating a modified PET with increased dyeing efficacy and improved binding to polyvinyl chloride without altering the polymer's bulk properties (4, 5).On the other hand, enzymatic hydrolysis of PET has the inherent disadvantage of occurring at a very low rate (5, 6). The reasons for this are not yet clearly understood. The access of the active center of the cutinase to the insoluble substrate is apparently one of the rate-limiting points, because enlarging the areas around the active sites of cutinases from Fus...