Poly(vinyl alcohol)/poly(acrylic acid) (PVA/PAA) nanofibers with the fiber diameter of 100–150 nanometers were fabricated by electrospinning. PVA/PAA nanofibers were crosslinked by heat‐induced esterification and resulting nanofiber mats insoluble in water. α‐Amylase was covalently immobilized onto the PVA/PAA nanofiber surfaces via the activation of amine groups in the presence of 1,1′‐carbonyldiimidazole. The immobilized α‐amylase has more resistance to temperature inactivation than that of the free form and showed maximum activity at 50°C. pH‐dependent activities of the free and immobilized enzymes were also investigated, and it was found that the pH of maximum activity for the free enzyme was 6.5, while for the optimal pH of the immobilized enzyme was 6.0. Reuse studies demonstrated that the immobilized enzyme could reuse 15 times while retaining 81.7% of its activity. Free enzyme lost its activity completely within 15 days. Immobilized enzyme lost only 17.1% of its activity in 30 days. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013

No abstract

No abstract

Proton-conductive electrospun nanofibers are promising potential materials for several advanced technological applications such batteries, sensors, and fuel cells. In this work, we prepared poly(vinyl butyral)/polyaniline (PVB/PANI) nanofibers via electrospinning and determined their proton conductivities. Structural characterization of the nanofibers was performed by FTIR analysis. Surface morphology of the nanofibers was determined by SEM and AFM. The addition of PANI significantly affected the fiber morphology, and over 90% reduction (with respect to neat PVB nanofibers) in the average nanofiber diameters was observed. Nanofiber mats were doped with polyphosphoric acid. The proton conductivity of the 2 wt.% PANI containing blend nanofibers was found as 18 × 10 −6 S/cm at room temperature and at 100% humidity. K E Y W O R D Satomic force microscopy, electrospinning, poly(vinyl butyral), polyaniline, proton conductivity