In this study, Au:TiO2 nanoparticles (NPs) are prepared by using the laser ablation method in liquid at different laser energies (600, 800, and1000 mJ). After that, Au: TiO2 NPs were deposited on porous-Si(PS). Porous silicon (PS) is synthesized by using the photoelectrochemical etching (PECE) of n-type crystalline Si (c-Si) wafers of (100) orientation. The intensity of the etching current density was (4, 12, and 20 mA/cm 2 ), with 16% (HF), and the etching time was 15 minutes. The X-ray diffraction (XRD) techniques, scanning electron microscopy (SEM), UV-visible spectrophotometry, and electrical properties are used to characterize the obtained particles. From the photo-detector measurements, the spectral responsivity curves three inclusive regions; the first peak was due to the absorption of UV light by Au: TiO2 NPs. The second peak was corresponding to the visible light absorption with the PS layer and the third peak was due to the absorption edge of the Si substrate. The higher responsivity of Au: TiO2 NPs/PS photo-detector was found to be 2.56A/W for specimens prepared at laser energy 800mJ.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.