were then exposed to demineralizing solution for 72 hours. Examination of slabs was performed using vickers microhardness test and scanning electron microscope; The lowest microhardness was recorded in group G, while inGL and GFL groups it significantly increased. Scanning electron microscope revealed a pronounced loss of central prism core and retention of prism peripheries in group G. Confluence of prismatic and interprismatic structures in GL slabs and irregular rough surface with prismatic boundaries conservation in GFL slabs were detected. Applying laser improved the microhardness and counteracted the adverse effect of gamma radiation. Adding fluoride before laser irradiation had a marked effect on microhardness..
Objective:The purpose of this study was to compare laser with conventional techniques in class V cavity preparation in gamma-irradiated teeth.Methods:Forty extracted human teeth with no carious lesions were used for this study and were divided into two main groups: Group I (n = 20) was not subjected to gamma radiation (control) and Group II (n=20) was subjected to gamma radiation of 60 Gray. Standard class V preparation was performed in buccal and lingual sides of each tooth in both groups. Buccal surfaces were prepared by the Er,Cr:YSGG laser (Waterlase iPlus) 2780 nm, using the gold handpiece with MZ10 Tip in non-contact and the “H” mode, following parameters of cavity preparation – power 6 W, frequency 50 Hz, 90% water and 70% air, then shifting to surface treatment laser parameters – power 4.5 W, frequency 50 Hz, 80% water and 50% air. Lingual surfaces were prepared by the conventional high-speed turbine using round diamond bur. Teeth were then sectioned mesio-distally, resulting in 80 specimens: 40 of which were buccal laser-treated (20 control and 20 gamma-irradiated specimens) and 40 were lingual conventional high-speed bur specimens (20 control and 20 gamma-irradiated specimens).Results:Microleakage analysis revealed higher scores in both gamma groups compared with control groups. Chi-square test revealed no significant difference between both control groups and gamma groups (p=1, 0.819, respectively). A significant difference was revealed between all 4 groups (p=0.00018).Conclusion:Both laser and conventional high-speed turbine bur show good bond strength in control (non-gamma) group, while microleakage is evident in gamma group, indicating that gamma radiation had a dramatic negative effect on the bond strength in both laser and bur-treated teeth.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.