Iron catalysts have been used widely for the mass production of carbon nanotubes (CNTs) with high yield. In this study, UV/visible spectroscopy was used to determine the Fe catalyst content in CNTs using a colorimetric technique. Fe ions in solution form red–orange complexes with 1,10-phenanthroline, producing an absorption peak at λ=510 nm, the intensity of which is proportional to the solution Fe concentration. A series of standard Fe solutions were formulated to establish the relationship between optical absorbance and Fe concentration. Many Fe catalysts were microscopically observed to be encased by graphitic layers, thus preventing their extraction. Fe catalyst dissolution from CNTs was investigated with various single and mixed acids, and Fe concentration was found to be highest with CNTs being held at reflux in HClO4/HNO3 and H2SO4/HNO3 mixtures. This novel colorimetric method to measure Fe concentrations by UV/Vis spectroscopy was validated by inductively coupled plasma optical emission spectroscopy, indicating its reliability and applicability to asses Fe content in CNTs.
This study investigated the effect of graphite nanoplatelet (GNP) size and dispersion on the thermal conductivities and tensile strengths of epoxy-based composites. GNPs of four different platelet sizes, ranging from 1.6 to 3 µm, were derived by mechanically exfoliating and breaking expanded graphite (EG) particles using high-energy bead milling and sonication. The GNPs were used as fillers at loadings of 0–10 wt%. As the GNP size and loading amount increased, the thermal conductivities of the GNP/epoxy composites increased, but their tensile strengths decreased. However, interestingly, the tensile strength reached a maximum value at the low GNP content of 0.3% and thereafter decreased, irrespective of the GNP size. Our observations of the morphologies and dispersions of the GNPs in the composites indicated that the thermal conductivity was more likely related to the size and loading number of fillers, whereas the tensile strength was more influenced by the dispersion of fillers in the matrix.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.