The use of replicative processes has become strategic and critical in industry to produce precise, microscopically detailed metallic parts and devices via low cost manufacturing routes. Metal powder hot embossing is an emerging process that brings some advantages associated with the reduction of production costs relative to powder injection moulding (PIM). The technology involves four distinct steps: preparation of the selected feedstock material (powder and binder); hot embossing; debinding; and sintering. The effect of continuous pressure during the hot embossing step as a means of replicating microdetails in 316L stainless steel parts is examined. Dimensional accuracy, microstructure and mechanical properties of the parts produced were evaluated. For the configuration tested, the most promising results were achieved when processing at 180°C for 30 min at a pressure of 14 MPa.
Hot embossing is a small-scale, low-cost processing technology that can deliver products to the market in a short time. This microreplication technology is well established to produce polymeric components and has applications in several industrial sectors. The use of micropowder hot embossing in the production of metal components is an emerging and challenging process that, when compared to other typical technologies, brings some economic advantages in a volatile market with an increasing tendency to manufacture customized products. The main objective of this review is to analyze the potential of powder hot embossing and its developments in the production of metallic microparts/components. This technology requires four distinct steps: (1) production feedstock (preparation of mixtures), (2) hot embossing (shape forming), (3) debinding and (4) sintering. These steps are interrelated and influence the characteristics of the final metallic microparts. This study summarizes the approaches implemented for the use of different metallic powders and polymeric binder systems for the preparation of the feedstock, the mold materials and the critical conditions tested in the embossing step to produce green parts, and the production of the final parts through the application of debinding and sintering. Powder hot embossing is a viable replication technology that allows the production of new metallic microcomponents, contributing to the global scientific effort of miniaturizing manufacturing process, equipment and products. The merit of powder hot embossing for industrialization needs further development to assert itself in the market and compete with other micromanufacturing techniques.
Ti-Si-CON films were deposited by DC reactive magnetron sputtering using different partial pressure of oxygen (p O2) and nitrogen (p N2) ratio. Compositional analysis revealed the existence of two different growth zones for the films; one zone deposited under low p O2 /p N2 and another zone deposited under high p O2 /p N2. The films produced under low p O2 /p N2 were deposited at a lower rate and presented a fcc structure, as well as, dense and featureless morphologies. The films deposited with high p O2 /p N2, consequently higher oxygen content, were deposited at a higher rate and developed an amorphous structure. The structural changes are consistent with the hardness and Young's modulus evolution, as seen by the significant reduction of the hardness and influence on the Young's modulus by increasing p O2 /p N2.
Additive manufacturing (AM) is one of the most trending technologies nowadays, and it has the potential to become one of the most disruptive technologies for manufacturing. Academia and industry pay attention to AM because it enables a wide range of new possibilities for design freedom, complex parts production, components, mass personalization, and process improvement. The material extrusion (ME) AM technology for metallic materials is becoming relevant and equivalent to other AM techniques, like laser powder bed fusion. Although ME cannot overpass some limitations, compared with other AM technologies, it enables smaller overall costs and initial investment, more straightforward equipment parametrization, and production flexibility.This study aims to evaluate components produced by ME, or Fused Filament Fabrication (FFF), with different materials: Inconel 625, H13 SAE, and 17-4PH. The microstructure and mechanical characteristics of manufactured parts were evaluated, confirming the process effectiveness and revealing that this is an alternative for metal-based AM.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.