Terahertz (THz) emission increase is observed for GaAs thin films that exhibit structural defects. The GaAs epilayers are grown by molecular beam epitaxy on exactly oriented Si (100) substrates at three different temperatures (Ts = 320ºC, 520ºC and 630ºC). The growth method involves the deposition of two low-temperature-grown (LTG)-GaAs buffers with subsequent in-situ thermal annealing at Ts = 600ºC. Reflection high energy electron diffraction confirms the layer-by-layer growth mode of the GaAs on Si. X-ray diffraction shows the improvement in crystallinity as growth temperature is increased. The THz time-domain spectroscopy is performed in reflection and transmission excitation geometries. At Ts = 320ºC, the low crystallinity of GaAs on Si makes it an inferior THz emitter in reflection geometry, over a GaAs grown at the same temperature on a semi-insulating GaAs substrate. However, in transmission geometry, the GaAs on Si exhibits less absorption losses. At higher Ts, the GaAs on Si thin films emerge as promising THz emitters despite the presence of antiphase boundaries and threading dislocations as identified from scanning electron microscopy and Raman spectroscopy. An intense THz emission in reflection and transmission excitation geometries is observed for the GaAs on Si grown at Ts = 520ºC, suggesting the existence of an optimal growth temperature for GaAs on Si at which the THz emission is most efficient in both excitation geometries. The results are significant in the growth design and fabrication of GaAs on Si material system intended for future THz photoconductive antenna emitter devices.
We report on the spintronic terahertz (THz) emission from a Ni/Pt bilayer on MgO grown via electron beam deposition. The films were grown with varying Ni thicknesses with a constant Pt thickness. The nominal Ni thickness values of 3, 5, 7, 9, 15, and 23 nm exhibited thickness-dependence of the THz emission intensities which was well-fitted with a model by Torosyan et al. Thickness-dependence was also observed for the peak frequencies and bandwidth characteristics. These results are consistent with previously reported MBE-grown ferromagnetic/nonmagnetic metal spintronic THz emitters utilizing the inverse spin-Hall effect.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.