The aims of the study were to evaluate the influence of pectin isolated from fireweed (FP) on the mechanical and rheological properties of agar (A) gel, to investigate the release of phenolic compounds (PCs) and pectin from A-FP gels at simulated digestion in vitro, and to evaluate the oral processing and sensory properties of A-FP gels. The hardness of A-FP gels decreased gradually with the increase in the concentration of FP added (0.1, 0.4, and 1.6%). The hardness of A-FP1.6 gel was 41% lower than A gel. Rheological tests found A gel was a strong physical gel (storage modulus (G′) >>loss modulus (G″)), and the addition of FP up to 1.6% did not significantly change its G’. The G″ value decreased in A-FP gels compared to A gel. The release of galacturonic acid (GalA) was 3.4 ± 0.5, 0.5 ± 0.2, 2.4 ± 1.0, and 2.2 ± 0.7 mg/mL after digestion of A-FP1.6 gel in the oral in vivo phase (OP) and subsequent incubation in simulated gastric (SGF), intestinal (SIF), and colonic (SCF) fluids in vitro. The incubation medium after OP, SGF, and SIF digestion of A-FP1.6 contained 24–64 μg GAE/mL of PCs, while SCF contained 144 μg GAE/mL, supposing a predominant release of antioxidant activity from the gel in the colon. Chewing to readiness for swallowing A-FP gel required less time and fewer chews with less activity of the masseter and temporalis muscles. A-FP1.6 gel had a lower likeness score for taste and consistency and a similar score for appearance and aroma when compared with A gel. Thus, A-FP gels were weakened compared to A gel and required less time and muscle activity for oral processing. A-FP gel had antioxidant activity due to the PCs associated with pectin, while A gel had no antioxidant activity.
The study aimed to compare the in vitro biocompatibility of pectin gels formed by different cross-linking cations. Hydrogel beads named CaPG, ZnPG, FePG, and AlPG were prepared from 4% solutions of apple pectin using ionotropic gelling with CaCl2, ZnCl2, FeCl3, and AlCl3, respectively. Cations influenced the gel strength of the wet gel beads in the following order (least strong) Ca2+ < Zn2+ < Fe3+~Al3+ (most strong). The swelling degree of the CaPG beads after 24 h of incubation in the RPMI-1640 medium was 104%, whereas the ZnPG, FePG, and AlPG beads swelled by 76, 108, and 134%, respectively. The strength of the pectin gel decreased significantly after incubation in the RPMI-1640 medium for 24 h, regardless of the cross-linking cation, although the FePG beads remained the strongest. All the pectin beads adsorbed serum proteins to a low degree, however the serum protein adsorption by the ZnPG and FePG beads (1.46 ± 0.87 and 1.35 ± 0.19 µg/mm2) was more than the CaPG and AlPG beads (0.31 ± 0.36 and 0.44 ± 0.25 µg/mm2). All the pectin beads reduced the production of TNF-α and IL-10 by hPBMCs in response to LPS stimulation. The IL-1β response of cells to LPS was significantly reduced by the CaPG, ZnPG, and FePG beads, whereas the AlPG beads enhanced it twofold. The CaPG, FePG, and AlPG beads had no cytotoxicity. The viability of hPBMCs and human fibroblasts incubated with ZnPG beads was 5.3 and 7.2%, respectively. Thus, the use of different cross-linking cations changed the properties of the pectin gel, which is important for biocompatibility.
This study aims to develop hydrogels from apple pectin (AP) and hogweed pectin (HP) in multiple ratios (4:0; 3:1; 2:2; 1:3; and 0:4) using ionotropic gelling with calcium gluconate. Rheological and textural analyses, electromyography, a sensory analysis, and the digestibility of the hydrogels were determined. Increasing the HP content in the mixed hydrogel increased its strength. The Young’s modulus and tangent after flow point values were higher for mixed hydrogels than for pure AP and HP hydrogels, suggesting a synergistic effect. The HP hydrogel increased the chewing duration, number of chews, and masticatory muscle activity. Pectin hydrogels received the same likeness scores and differed only in regard to perceived hardness and brittleness. The galacturonic acid was found predominantly in the incubation medium after the digestion of the pure AP hydrogel in simulated intestinal (SIF) and colonic (SCF) fluids. Galacturonic acid was slightly released from HP-containing hydrogels during chewing and treatment with simulated gastric fluid (SGF) and SIF, as well as in significant amounts during SCF treatment. Thus, new food hydrogels with new rheological, textural, and sensory properties can be obtained from a mixture of two low-methyl-esterified pectins (LMPs) with different structures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.